# US 5,597,640 A · Oriented plastic strap > Agents: this data is available as JSON from the patentgrep API and MCP server — see https://patentgrep.com/llms.txt - Number: US 5,597,640 A - Document ID: US5597640A - Status: Granted - Kind: A - Application number: 08/528,286 - Filed: 1995-09-14 - Granted: 1997-01-28 - Earliest claimed: 1992-10-09 - Assignees: Signode Corporation - Inventors: Donald L. Van Erden; Manuel C. Enriquez; Hans Weltekamper - Web page: https://patentgrep.com/patent/US5597640A ## CPC - B29C 55/065: {in several stretching steps} - B29C 43/24: Calendering - B29C 55/06: parallel with the direction of feed - B29C 55/18: by squeezing between surfaces, e.g. rollers - B29K 2067/00: Use of polyesters {or derivatives thereof}, as moulding material - B29L 2007/007: {Narrow strips, e.g. ribbons, tapes, bands (belts B29L2029/00; tapes as carrier of sound or information B29L2017/008)} - Y10T 428/24107: including mechanically interengaged strands, strand-portions or strand-like strips - Y10T 428/24405: Polymer or resin [e.g., natural or synthetic rubber, etc.] - Y10T 428/24777: Edge feature - Y10T 428/266: of base or substrate - Y10T 428/31: Surface property or characteristic of web, sheet or block - Y10T 428/31504: Composite [nonstructural laminate] - B29C: SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING (making preforms B29B11/00; making laminated products by combining previously unconnected layers which become one product whose layers will remain together B32B37/00 - B32B41/00) - B29K: INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR {MOULDS, } REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS - B29L: INDEXING SCHEME ASSOCIATED WITH SUBCLASS B29C, RELATING TO PARTICULAR ARTICLES - Y10T: TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION ## Abstract An apparatus and method for producing an oriented plastic strap having a predetermined desired thickness for use in connection with the strapping of packages or the like, is disclosed. A sheet workpiece is conducted into a nip defined between a pair of milling and stretching rollers wherein one of the rollers is rotated at a lineal surface velocity which is greater than the lineal surface velocity of the other roller, and the rollers are rotated in opposite directions. One of the rollers effectively brakes or retards one of the surfaces of the sheet workpiece while the other one of the rollers effectively accelerates the other one of the surfaces of the sheet workpiece as the workpiece passes through the nip defined between the rollers whereby the workpiece is simultaneously milled and stretched. Additional heating is provided in connection with the surface of the sheet workpiece which is exposed to the ambient air prior to entry of the workpiece into the nip defined between the pair of rollers such that both surfaces will have similar temperature levels so as to exhibit similar density properties, and still further, the edge portions of the sheet workpiece are also heated so as to advantageously control the degree of flatness of the sheet material or workpiece across the width thereof. The flatness quality of the sheet workpiece can also be achieved through means of specially contoured milling rollers defining the zero gap assembly nip, or by means of specially contoured extrusion dies, whereby the edge portions are rendered thinner as compared to the central portion of the sheet workpiece such that upon milling and stretching of the workpiece, which operations tend to thicken the edge portions of the sheet workpiece, the edge portions will exhibit thickness dimensions commensurate with the thickness dimension of the central portion of the sheet workpiece. ## Claims ### Claim 1 A plastic strap made from a solid sheet of material having a predetermined original thickness dimension and simultaneously milled and stretched by being passed through a nip defined between a pair of opposed rollers which are spaced apart with respect to each other so as to define said nip therebetween which has a predetermined space dimension which is substantially less than said predetermined original thickness dimension of said solid sheet of material, and wherein said pair of opposed rollers are rotated in opposite directions at different lineal surface velocities, comprising: first surface means of said solid sheet of material for engaging a first circumferential portion of a first one of said pair of opposed rollers at a position upstream of said nip defined between said pair of opposed rollers and having a first predetermined temperature value; and second surface means of said solid sheet of material disposed out of contact with said first one of said pair of opposed rollers and having a second predetermined temperature value, at said position upstream of said nip defined between said pair of opposed rollers, which is greater than said first predetermined temperature value of said first surface means such that when said first and second surface means of said solid sheet of material reach said nip defined between said opposed rollers so as to be simultaneously milled and stretched by being passed through said nip defined between said pair of opposed rollers, said temperature values of said first and second surface means of said solid sheet of material will be substantially the same such that the density of said solid sheet of material across the thickness dimension of said solid sheet of material is substantially uniform. ### Claim 2 A plastic strap made from a solid sheet of material having a predetermined original thickness dimension and simultaneously milled and stretched by being passed through a nip defined between a pair of opposed rollers which are spaced apart with respect to each other so as to define said nip therebetween which has a predetermined space dimension which is substantially less than said predetermined original thickness dimension of said solid sheet of material, and wherein said pair of opposed rollers are rotated in opposite directions at different lineal surface velocities, comprising: a solid sheet of material for engaging a first circumferential portion of a first one of said pair of opposed rollers, for passing through said nip so as to be simultaneously milled and stretched within said nip defined between said pair of opposed rollers, and for engaging a second circumferential portion of a second one of said pair of opposed rollers; and opposite heated edge portions of said solid sheet of material disposed upstream of said nip defined between said pair of opposed rollers so as to increase the degree of flatness of said simultaneously milled and stretched solid sheet of material across the width of said simultaneously milled and stretched solid sheet of material after said simultaneously milled and stretched solid sheet of material has passed through said nip defined between said pair of opposed rollers. ### Claim 3 A plastic strap made from a solid sheet of material which is simultaneously milled and stretched by being passed through a nip defined between a pair of opposed rollers which are spaced apart with respect to each other so as to define said nip therebetween which has a predetermined space dimension, and wherein said pair of opposed rollers are rotated in opposite directions at different lineal surface velocities, comprising: a solid sheet of material having a central portion having a predetermined original thickness dimension which is greater than said predetermined space dimension of said nip defined between said pair of opposed rollers; and said solid sheet having opposite edge portions which have a thickness dimension which is less than said predetermined original thickness dimension of said central portion of said solid sheet of material such that an increased degree of flatness of said simultaneously milled and stretched solid sheet of material across the width of said simultaneously milled and stretched solid sheet of material after said simultaneously milled and stretched solid sheet of material has passed through said nip defined between said pair of opposed rollers is achieved as a result of thickening of said opposite edge portions of said solid sheet of material due to said simultaneous milling and stretching thereof within said nip defined between said pair of opposed rollers. ### Claim 4 (depends on 1) A plastic strap as set forth in claim 1, wherein: said second predetermined temperature value of said second surface means is approximately 242.degree. F. ### Claim 5 (depends on 1) A plastic strap as set forth in claim 1, wherein: said temperature values of said first and second surface means of said solid sheet of material, at said nip defined between said opposed rollers, will both be approximately 236.degree. F. ### Claim 6 (depends on 1) A plastic strap as set forth in claim 1, wherein: said solid sheet of material comprising said strap after being passed through said nip defined between said pair of opposed rollers has a finalized thickness dimension which is less than said predetermined space dimension of said nip as defined between said pair of opposed, oppositely rotating rollers. ### Claim 7 (depends on 1) A plastic strap as set forth in claim 1, wherein: said solid sheet of material comprises polypropylene. ### Claim 8 (depends on 1) A plastic strap as set forth in claim 1, wherein: said strap exhibits tensile strength characteristics which are substantially greater than tensile strength characteristics of conventional straps produced by processes comprising non-simultaneous milling and stretching, wherein said tensile strength characteristics of said conventional straps comprise a maximum value of 45,000 psi. ### Claim 9 (depends on 8) A plastic strap as set forth in claim 8, wherein: said tensile strength characteristics of said strap comprises a value of 64,000 psi. ### Claim 10 (depends on 8) A plastic strap as set forth in claim 8, wherein: said strap exhibits split resistance characteristics which are substantially less than split resistance characteristics of said conventional straps when said tensile strength characteristics of said strap are greater than said maximum tensile strength value of 45,000 psi characteristic of said conventional straps. ### Claim 11 (depends on 10) A plastic strap as set forth in claim 10, wherein: said split resistance of said strap comprises 0.07 inches when said tensile strength value of said strap comprises 64,000 psi. ### Claim 12 (depends on 2) A plastic strap as set forth in claim 2, wherein: said solid sheet of material comprising said strap after being passed through said nip defined between said pair of opposed rollers has a finalized thickness dimension which is less than said predetermined space dimension of said nip as defined between said pair of opposed, oppositely rotating rollers. ### Claim 13 (depends on 2) A plastic strap as set forth in claim 2, wherein: said solid sheet of material comprises polypropylene. ### Claim 14 (depends on 2) A plastic strap as set forth in claim 2, wherein: said strap exhibits tensile strength characteristics which are substantially greater than tensile strength characteristics of conventional straps produced by processes comprising non-simultaneous milling and stretching, wherein said tensile strength characteristics of said conventional straps comprise a maximum value of 45,000 psi. ### Claim 15 (depends on 14) A plastic strap as set forth in claim 14, wherein: said tensile strength characteristics of said strap comprises a value of 64,000 psi. ### Claim 16 (depends on 14) A plastic strap as set forth in claim 14, wherein: said strap exhibits split resistance characteristics which are substantially less than split resistance characteristics of said conventional straps when said tensile strength characteristics of said strap are greater than said maximum tensile strength value of 45,000 psi characteristic of said conventional straps. ### Claim 17 (depends on 16) A plastic strap as set forth in claim 16, wherein: said split resistance of said strap comprises 0.07 inches when said tensile strength value of said strap comprises 64,000 psi. ### Claim 18 (depends on 2) A plastic strap as set forth in claim 2, wherein: said simultaneously milled and stretched solid sheet of material has a widthwise dimension of approximately twenty-four inches (24"); and said simultaneously milled and stretched solid sheet of material has a substantially uniform degree of flatness across said width thereof except for thickened side edge portions thereof which have a width dimension of approximately one-half inch (0.5") . ### Claim 19 (depends on 3) A plastic strap as set forth in claim 3, wherein: said solid sheet of material, prior to entering said nip defined between said pair of opposed rollers, has a substantially trapezoidal configuration as viewed in cross-section. ### Claim 20 (depends on 3) A plastic strap as set forth in claim 3, wherein: said solid sheet of material comprising said strap after being passed through said nip defined between said pair of opposed rollers has a finalized thickness dimension which is less than said predetermined space dimension of said nip as defined between said pair of opposed, oppositely rotating rollers. ### Claim 21 (depends on 3) A plastic strap as set forth in claim 3, wherein: said solid sheet of material comprises polypropylene. ### Claim 22 (depends on 3) A plastic strap as set forth in claim 3, wherein: said strap exhibits tensile strength characteristics which are substantially greater than tensile strength characteristics of conventional straps produced by processing comprising non-simultaneous milling and stretching, wherein said tensile strength characteristics of said conventional straps comprise a maximum value of 45,000 psi. ### Claim 23 (depends on 22) A plastic strap as set forth in claim 22, wherein: said tensile strength characteristics of said strap comprises a value of 64,000 psi. ### Claim 24 (depends on 22) A plastic strap as set forth in claim 22, wherein: said strap exhibits split resistance characteristics which are substantially less than split resistance characteristics of said conventional straps when said tensile strength characteristics of said strap are greater than said maximum tensile strength value of 45,000 psi characteristic of said conventional straps. ### Claim 25 (depends on 24) A plastic strap as set forth in claim 24, wherein: said split resistance of said strap comprises 0.07 inches when said tensile strength value of said strap comprises 64,000 psi.