Asphalt improvement
AssigneeAshland Inc.
InventorRoger E. Hayner
Life of this patent
Estimating the term…
Abstract
Novel compositions comprising asphalt, having improved durability, are disclosed, the compositions comprising or containing (a) from about 0.1 percent to about 5.0 percent of a metal hydrocarbyldithiophosphate, or mixture thereof, and (b) from about 0.1 percent to about 5.0 percent of an antioxidant butylated phenol, or mixture thereof, the ratio of (a) to (b) being from about 0.75:1 to about 4.0:1. A process of making such improved compositions is also described, as well as methods of utilizing such compositions.
Claims34
A composition comprising an asphalt composition containing an oxidation inhibiting amount of (a) a metal hydrocarbyldithiophosphate, or mixture thereof, and (b) an antioxidant butylated phenol, or mixture thereof, the ratio of (a) to (b) being from about 0.75:1 to about 4.0:1.
A process for improving the durability of an asphalt composition comprising blending with said asphalt composition, at a temperature sufficient to liquefy said paving asphalt composition, an oxidation inhibiting amount of (a) a metal hydrocarbyldithiophosphate, or mixture thereof, and (b) an antioxidant butylated phenol, or mixture thereof, the ratio of the Group II metal hydrocarbyldithiophosphate, or mixture thereof, to the antioxidant butylated phenol, or mixture thereof, being from about 0.75:1 to about 4.0:1.
A composition comprising an asphalt composition containing (a) from about 0.1 percent to about 5.0 percent of a composition selected from metal hydrocarbyldithiophosphates, and mixtures thereof, and (b) from about 0.1 percent to about 5.0 percent of a composition selected from antioxidant butylated phenols, and mixtures thereof, the ratio of (a) to (b) being from about 0.75:1 to about 4.0:1.
A pavement composition comprising aggregate and from about 1.0 percent to about 10.0 percent of a paving asphalt composition containing an oxidation inhibiting amount of (a) a metal hydrocarbyldithiophosphate, or mixture thereof, and (b) an antioxidant butylated phenol, or mixture thereof, the ratio of (a) to (b) being from about 0.75:1 to about 4.0:1.
A process for improving the durability of an asphalt composition comprising blending with said asphalt composition, at a temperature sufficient to liquefy said asphalt composition, from about 0.1 percent to about 5.0 percent of a composition selected from metal hydrocarbyldithiophosphates, and mixtures thereof, and from about 0.1 percent to about 5.0 percent of a composition selected from antioxidant butylated phenols, and mixtures thereof, the ratio of the metal hydrocarbyldithiophosphate, or mixture thereof, to the antioxidant butylated phenol, or mixture thereof, being from about 0.75:1 to about 4.0:1.
An asphalt composition containing an oxidation inhibiting amount of (a) a metal hydrocarbyldithiophosphate, or mixture thereof, and (b) an antioxidant butylated phenol, or mixture thereof, the ratio of (a) to (b) being from about 0.75:1 to about 4.0:1.
An asphalt composition containing (a) from about 0.1 percent to about 5.0 percent of a metal hydrocarbyldithiophosphate, or mixture thereof, and (b) from about 0.1 percent to about 5.0 percent of an antioxidant butylated phenol, or mixture thereof, the ratio of (a) to (b) being from about 0.75:1 to about 4.0:1.
An asphalt composition containing (a) from about 0.1 percent to about 2.0 percent of a metal hydrocarbyldithiophosphate, or mixture thereof, and (b) from about 0.1 percent to about 2.0 percent of an antioxidant butylated phenol, or mixture thereof, the ratio of (a) to (b) being from about 1.5:1 to about 4.0:1.
A process for improving the durability of a paving asphalt composition comprising blending with said asphalt composition, at a temperature sufficient to liquefy said paving asphalt composition, from about 0.1 percent to about 2.0 percent of a metal hydrocarbyldithiophosphate, or mixture thereof, and from about 0.1 percent to about 2.0 percent of an antioxidant butylated phenol, or mixture thereof, the ratio of said hydrocarbyldithiophosphate to said antioxidant phenol being from about 0.75:1 to about 4.0:1.
A pavement composition comprising aggregate and from about 1.0 percent to about 10.0 percent of a paving asphalt composition containing (a) from about 0.1 percent to about 5.0 percent of a composition selected from metal hydrocarbyldithiophosphates, or mixtures thereof, and (b) from about 0.1 percent to about 5.0 percent of a composition selected from antioxidant butylated phenols, or mixtures thereof, the ratio of (a) to (b) being from about 0.75:1 to about 4.0.:1.
A method for paving comprising
- heating paving asphalt sufficiently to liquefy said paving asphalt, and forming liquefied paving asphalt;
- blending with said liquefied paving asphalt (a) from about 0.1 percent to about 5.0 percent of a composition selected from metal hydrocarbyldithiophosphates, and mixtures thereof, and (b) from about 0.1 percent to about 5.0 percent of a composition selected from antioxidant butylated phenols, and mixtures thereof, the ratio of (a) to (b) being from about 0.75:1 to about 4.0:1, forming a liquefied modified paving asphalt;
- mixing aggregate with said liquefied modified paving asphalt to form an aggregate-modified asphalt paving mixture;
- distributing aggregate-modified asphalt paving mixture over a surface to be paved;
- and
- compacting distributed aggregate-modified asphalt paving mixture to the desired density to produce a laydown of asphalt concrete.
A method for paving comprising
- heating a modified paving asphalt containing (a) from about 0.1 percent to about 5.0 percent of a composition selected from Group II metal hydrocarbyldithiophosphates, and mixtures thereof, and (b) from about 0.1 percent to about 5.0 percent of a composition selected from antioxidant butylated phenols, and mixtures thereof, the ratio of (a) to (b) being from about 0.75:1 to about 4.0:1, sufficiently to liquefy said paving asphalt, and forming liquefied modified paving asphalt;
- mixing aggregate with liquefied modified paving asphalt to form an aggregate-modified asphalt paving mixture;
- distributing aggregate-modified asphalt paving mixture over a surface to be paved;
- and
- compacting distributed aggregate-modified asphalt paving mixture to the desired density to produce a laydown of asphalt concrete.
A method for paving comprising
- forming a gel of a liquefied modified paving asphalt containing (a) from about 0.1 percent to about 5.0 percent of a composition selected from metal hydrocarbyldithiophosphates, and mixtures thereof, and (b) from about 0.1 percent to about 5.0 percent of a composition selected from antioxidant butylated phenols, and mixtures thereof, the ratio of (a) to (b) being from about 0.75:1 to about 4.0:1;
- removing water of reaction from the gel, forming substantially water-free gelled modified paving asphalt;
- mixing aggregate with gelled liquefied modified paving asphalt to form an aggregate-modified asphalt paving mixture;
- distributing aggregate-modified asphalt paving mixture over a surface to be paved;
- and
- compacting distributed aggregate-modified asphalt paving mixture to the desired density to produce a laydown of asphalt concrete.
A roofing composition comprising
- one or more layers of a water impervious material;
- and at least one layer of a roofing asphalt containing (a) from about 0.1 percent to about 5.0 percent of metal hydrocarbyldithiophosphate, or mixture thereof, and (b) from about 0.1 percent to about 5.0 percent of an antioxidant butylated phenol, or mixture thereof, the ratio of (a) to (b) being from about 0.75:1 to about 4.0:1, applied to said water impervious material.
A method of roofing comprising
- applying one or more layers of a water impervious material to an external roof surface;
- distributing at least one layer of a roofing asphalt containing (a) from about 0.1 percent to about 5.0 percent of a composition selected from metal hydrocarbyldithiophosphates, and mixtures thereof, and (b) from about 0.1 percent to about 5.0 percent of a composition selected from antioxidant butylated phenols, and mixtures thereof, the ratio of (a) to (b) being from about 0.75:1 to about 4.0:1, to the surface of the water impervious material not in contact with the external roof surface.
Dependencies are inferred from the claim text.