Abstract
A materials system comprising a glass containing alkali metal ions capable of migrating and a silica, alumina, or tantala film deposited on the glass surface, the glass also containing high field strength ions that can change coordination. The direction of alkali metal ion flow depends on the film selected and the glass composition.
Claims18
A materials system comprising a barrier layer oxide film selected from the group consisting of silica, alumina and tantala films deposited on a glass surface, the glass having a content of mobile alkali metal ions and a composition containing a sufficient amount of high field strength ions that can change coordination so that the following expressions, in cation percent values,
- P.sup.1 =[Na.sup.+ +Li.sup.+ +K.sup.+ +Cs.sup.+ +Rb.sup.+ ]+2[Sr.sup.2+ +Ba.sup.2+ +Ca.sup.2+ /2]-[Al.sup.3+ ], in conjunction with an alumina or tantala film, and
- P=P.sup.1 -0.6[B.sup.3+ ]-[Zn.sup.2+ +Be.sup.2+ +Mg.sup.2+ +Ca.sup.2+ /2] in conjunction with a silica film, are negative, whereby the direction of any flow of a migrating alkali metal ion is toward the glass.
An LCD device having a glass panel with a barrier layer oxide film selected from the group consisting of silica, alumina and tantala films deposited on a surface of the panel, the glass having a content of mobile alkali metal ions and also containing a sufficient amount of high field strength ions that can change coordination so that the expressions, in cation percent values
- P.sup.1 =[Na.sup.+ +Li.sup.+ +K.sup.+ +Cs.sup.+ +Rb.sup.+ ]+2[Sr.sup.2+ +Ba.sup.2+ +Ca.sup.2+ /2]-[Al.sup.3+ ] in conjunction with an alumina or tantala film, and
- P=P.sup.1 -0.6 [B.sup.3+ ]-[Zn.sup.2+ +Be.sup.2+ +Mg.sup.2+ +Ca.sup.2+ /2] in conjunction with a silica film, are negative, whereby any flow of a migrating alkali metal ion is in the direction of the glass panel and the device is protected from alkali metal contamination.
A method of preventing the migration of alkali metal ions from a glass surface which comprises depositing a barrier layer oxide film selected from the group consisting of silica, alumina and tantala films on a glass containing high field strength ions that can change coordination, alkali metal ion flow being toward a glass having an alumina or tantala film being applied in combination with a glass having a composition such that the expression, in cation percent,
- P.sup.1 =[Na.sup.+ +Li.sup.+ +K.sup.+ +Cs.sup.+ +Rb.sup.+ ]+2[Sr.sup.2+ +Ba.sup.2+ +Ca.sup.2+ /2]-[Al.sup.3+ ], is negative, and toward a silica film being applied in combination with a glass having a composition such that the expression
- P=P.sup.1 -0.6[B.sup.3+ ]-[Zn.sup.2+ +Be.sup.2+ +Mg.sup.2+ +Ca.sup.2+ /2], is negative.
A method of protecting a material from alkali metal ion contamination when the material is in contact with a glass containing migratory alkali metal ions which comprises applying a barrier layer oxide film selected from the group consisting of silica, alumina and tantala films to a glass containing high field strength ions that change coordination in sufficient amount so that the expressions, in cation percent values
- P.sup.1 =[Na.sup.+ +Li.sup.+ +K.sup.+ +Cs.sup.+ +Rb.sup.+ ]+2[Sr.sup.2+ +Ba.sup.2+ +Ca.sup.2+ /2]-[Al.sup.3+ ], is negative when an alumina or tantala film is applied, and
- P=P.sup.1 -0.6[B.sup.3+ ]-[Zn.sup.2+ +Be.sup.2+ +Mg.sup.2+ +Ca.sup.2+ /2], is negative, when a silica film is applied to the glass surface in contact with the material being protected.