Method for preparing a nonwoven web containing antimicrobial siloxane quaternary ammonium salts

A method for preparing a nonwoven web having antimicrobal properties which comprises:

• melting a melt-extrudable thermoplastic composition:
• extruding the molten composition through multiple orifices to form streams of molten composition;
• cooling the streams of molten composition to form fibers;
• and
• randomly depositing said fibers on a moving foraminous surface to form a web;
• wherein
• said melt-extrudable thermoplastic composition at least one thermoplastic polyolefin which contains only hydrogen and carbon atoms and at least one additive which is adapted to surface segregate upon extrusion of the molten composition to impart antimicrobial properties to the surface of said fibers of which said nonwoven web is comprised wherein said additive has either the general formula A, ##STR21## wherein:
• (1) each of R.sub.1 -R.sub.7 is independently selected from the group consisting of monovalent C.sub.1 -C.sub.20 alkyl, phenyl, and phenyl-substituted C.sub.1 -C.sub.20 alkyl groups, in which each phenyl can be substituted or unsubstituted;
• (2) each of R.sub.8 and R.sub.9 is a monovalent group independently selected from the group consisting of (a) hydrogen and (b) monovalent alkyl, cycloalkyl, aryl, and heterocyclic groups and combinations thereof having up to about 30 carbon atoms, except that both R.sub.8 and R.sub.9 cannot be hydrogen;
• or, when taken together in combination with the carbon atom to which they are attached, R.sub.8 and R.sub.9 represent a carbonyl group;
• (3) each of R.sub.10 and R.sub.11 is a methyl group;
• (4) a represents an integer from 1 to about 20;
• (5) b represents an integer from 1 to about 20;
• (6) Z is a monovalent group having from about 8 to about 30 carbon atoms and selected from the group consisting of alkyl, cycloalkyl, aryl, and heterocyclic groups, and combinations thereof, wherein Z is terminated by an alkyl moiety which includes at least about 8 carbon atoms in a single continuous chain;
• (7) Y.sub.1 is an anion which does not cause the thermal instability of the additive to be more than about 35 wt. % decomposition during melt extrusion;
• and
• (8) said additive has a molecular weight of from about 600 to about 1,700;
• or the general formula B, ##STR22## wherein:
• (1) each of R.sub.20 -R.sub.23 is independently selected from the group consisting of monovalent C.sub.1 -C.sub.20 alkyl, phenyl, and phenyl-substituted C.sub.1 -C.sub.20 alkyl groups, in which each phenyl can be substituted or unsubstituted;
• (2) n represents an integer of from 1 to about 19;
• (3) each of Q.sub.1 and Q.sub.2 represents an independently selected quaternary ammonium group having the general formula, ##STR23## in which:
• (a) R.sub.24 is a monovalent alkyl group having from about 8 to about 30 carbon atoms, at least about 8 carbon atom of which make up a single continuous chain;
• (b) R.sub.25 and R.sub.26 are methyl groups;
• (c) each of R.sub.27 and R.sub.28 is a monovalent group independently selected from the group consisting of (i) hydrogen and (ii) monovalent alkyl, cycloalkyl, aryl, and heterocyclic groups and combinations thereof having up to about 30 carbon atoms, except that both R.sub.27 and R.sub.28 cannot be hydrogen;
• or, when taken together in combination with the carbon atom to which they are attached, R.sub.27 and R.sub.28 represent a carbonyl group;
• (d) c represents an integer of from 2 to about 20;
• and
• (e) d represents an integer of from 2 to about 20;
• (4) Y.sub.2 represents an anion which does not cause the thermal instability of the additive to be more than about 35 wt. % decomposition during melt extrusion;
• and
• (5) said additive has a polydispersity of up to about 3.0 and a weight-average molecular weight of from about 800 to about 2,000;
• wherein said additive is present in said melt-extrudable thermoplastic composition in an amount sufficient to impart antimicrobial activity to the surfaces of said fibers of which said nonwoven web is comprised.