Compositions which set in the presence of water and their use
AssigneeHilti Aktiengesellschaft
InventorsUlrich Hense, Peter Mauthe, Rudolf Hinterwaldner
Life of this patent
Estimating the term…
Abstract
A 2-component composition is disclosed which contains an inorganic binder as well as a curing agent composed of water or an aqueous solution. The composition also contains substances which regulate solidification and curing, as well as, if necessary, conventional amounts of slag powders, fillers and blowing agents. The composition is distinguished by the fact that it cures rapidly even at low temperatures and can be used in small amounts. As a result, the composition is particularly suitable as a dowelling composition for fastening anchor rods in boreholes.
Claims6
A curable inorganic dowelling composition for fastening anchor rods in boreholes, consisting essentially of:
- A) 32.5-73% by weight of an inorganic binder comprising:
- a1) finely divided SiO.sub.2 or its mixture with Al.sub.2 O.sub.3, containing at least 5% by weight of SiO.sub.2 ;
- a2) optionally aluminum silicate selected from the group consisting of kaolinite and metakaolinite;
- and
- a3) a hydraulic binder;
- B) 20-32.5% by weight of a curing agent selected from
- b1) water, and
- b2) an aqueous solution of alkali metal silicate, ammonium silicate, alkali metal oxide, ammonium hydroxide, amorphous silicic acid or any combination thereof;
- C) a curing accelerator selected from a member of the group consisting of CaO, MgO, Alite clinker phase (C.sub.3 S), tricalcium aluminate clinker phase (C.sub.3 A), CaC2;
- and
- D) a compound selected from the group consisting of a filler, blowing agent and any combination thereof.
A dowelling composition for fastening anchor rods in boreholes consisting essentially of a mixture containing, in the presence of water,
- 2.5% to 5% by weight of kaolinite, metakaolinite or a combination thereof;
- 30.3-68% by weight of a stone-forming inorganic binder selected from the group consisting of finely divided SiO.sub.2 and hydraulic binder;
- 2.5-30% by weight of a curing agent;
- 0.1-5.4% by weight of a curing accelerator selected from a member of the group consisting of CaO, MgO, Alite clinker phase (C.sub.3 S), tricalcium aluminate clinker phase (C.sub.3 A), CaC.sub.2 ;
- and
- the remainder being selected from the group consisting of a filler, foaming agent and a combination thereof.
Dependencies are inferred from the claim text.