Abstract
A method for forming a gas-filled consolidated metal billet, involving preparing a metallic shell container, filling the shell with a metal core material and pressurized gas, and consolidating the shell and its contents to form the billet. The consolidated billet is further formed in the same manner as solid metal components by conventional wrought mill working technologies. After thus forming a shaped billet having a predetermined, desired geometry, it is subjected to a heat treatment that expands the gas trapped within the core, to produce in situ a metal body having an integral sandwich-type structure with a solid metal facing and a porous metal core.
Claims11
A method for preparing a structural metal body having a sandwich structure comprising an integral porous internal metal core and a solid external metal facing, comprising:
- a. preparing an outer shell container from a solid metal material;
- b. filling the shell container with a plurality of internal metal core elements for forming the internal core structure;
- c. filling the core-filled shell container with a gas which is substantially unreactive with the internal metal core elements and the outer shell;
- d. sealing the gas-filled, core-filled shell container;
- e. applying heat and pressure to the sealed container to effect flow and diffusion bonding of the internal metal core elements to one another and to the outer shell, to consolidate the core elements and the shell into a dense, solid metal billet free of any permanent pore structure;
- f. heating and forming the consolidated billet into a shaped billet having a predetermined, desired geometry, to enhance metallurgical bonding between the core metal constituents and between the core and the shell;
- and
- g. heating the shaped billet to expand the gas trapped in the core and produce in situ the integral sandwich-type structure having a core comprising a permanent porous metallic structure and, integral therewith, a solid metal facing thereon.
A method for preparing a structural metal body having a sandwich structure comprising an integral porous internal metal core and a solid external metal facing, comprising:
- a. preparing an outer shell container from a titanium/aluminum/vanadium metal alloy;
- b. filling the shell container with a blend of elemental particulates of titanium sponge fines and aluminum-vanadium master alloy particulate in the same approximate weight ratio as said titanium/aluminum/vanadium alloy, for forming the internal core structure;
- c. vacuum-evacuating the particulate-filled shell container to a pressure of from approximately 10.sup.-2 to 10.sup.-5 torr;
- d. filling the shell container with argon at a pressure of from approximately 1 to 6 atmospheres;
- e. sealing the gas-filled, core-filled shell container to create a pressure-tight container;
- f. isostatically pressing the sealed, filled shell container at a temperature of from approximately 1650.degree. to 1800.degree. F. and a pressure of from approximately 10,000 to 25,000 psi, for a period of from approximately 1 to 3 hours to effect flow and diffusion bonding of the internal metal core elements to one another and to the outer shell and thereby consolidate the core elements and the shell into a dense, solid metal billet free of any permanent pore structure;
- g. rolling the consolidated metal billet and forming a sheet-like shaped billet using a rolling schedule appropriate for said titanium/aluminum/vanadium alloy, to enhance metallurgical bonding between the core metal constituents and between the core and the shell;
- h. forming the shaped billet into a metal sheet having a predetermined desired geometry;
- and
- i. heating the formed metal sheet at a temperature from approximately 1650.degree. to 2500.degree. F. for a period of from approximately 4 to 48 hours to expand the gas trapped in the core and produce a formed metal sheet comprising the integral sandwich structure having a core comprising a permanent porous metallic structure and, integral therewith, a solid metal facing thereon.