Process for upgrading low-quality wood
AssigneeShell Oil Company
InventorsPeter C. Rem, Hans van der Poel, Herman P. Ruyter
Life of this patent
Estimating the term…
Abstract
A process for upgrading low-quality wood to high-quality wood comprising the following stages: a) softening the wood by directly heating it electrically in the presence of a softening agent at a pressure of at least the equilibrium vapor pressure of the softening agent at the operating temperature; b) drying the softened wood; c) curing the dried wood; and d) cooling the cured wood.
Claims15
A process for upgrading low-quality wood to high-quality wood comprising the following stages:
- a. softening the low-quality wood by directly heating it electrically in the presence of an aqueous medium at a pressure of at least the equilibrium vapor pressure of the aqueous medium;
- b. drying the softened wood, wherein the drying stage comprises a first part and a second part;
- c. curing the dried wood;
- and
- d. cooling the cured wood, wherein the softening stage and at least the first part of the drying stage are carried out by ohmic heating.
A process for upgrading low-quality wood to high-quality wood comprising the following stages:
- a. softening the low quality wood by directly heating it dielectrically to a temperature in the range of from about 160.degree. C. to about 220.degree. C. for a period of time from about 1 minute to about 2 hours in the presence of an aqueous medium comprising water at a pressure of at least the equilibrium vapor pressure of the aqueous medium at the operating temperature;
- b. drying the softened wood in a first part and a second part by heating it dielectrically;
- c. curing the dried wood;
- and
- d. cooling the cured wood.
A process for upgrading low-quality wood to high-quality wood comprising the following steps:
- a. softening the low-quality wood by directly heating said wood by ohmic heating at an applied voltage in the range of from about 10 V/cm to about 200 V/cm in the presence of water at a pressure of at least the equilibrium vapor pressure of water at the operating temperature of from about 160.degree. C. to about 220.degree. C. for a period of time from about 1 minutes to about 2 hours;
- b. drying the softened wood wherein said drying is carried out in a first part and a second part, said drying in said first part comprising ohmic heating the wood at a temperature in the range of from about 100.degree. C. to about 220.degree. C. and a pressure in the range of from about 1 bar to about 20 bar and said drying in said second part comprising dielectric heating while applying an external mechanical pressure in the range of from about 0.1 bar to about 10 bar to said wood;
- c. curing the dried wood at a temperature in the range of from about 160.degree. C. to about 200.degree. C., a pressure in the range of from about 1 bar to about 20 bar and during a period of time in the range of from about 20 minutes to about 90 minutes;
- and
- d. cooling the cured wood.
A process for upgrading low-quality wood to high-quality wood comprising the following steps:
- a. softening the low-quality wood by directly heating said wood by dielectric heating in the presence of water at a pressure of at least the equilibrium vapor pressure of water at the operating temperature of from about 160.degree. C. to about 220.degree. C. for a period of time from about 1 minutes to about 2 hours;
- b. drying the softened wood at a temperature range of from about 90.degree. C. to about 200.degree. C. and a pressure in the range of from about 1 bar to about 20 bar;
- c. curing the dried wood at a temperature in the range of from about 160.degree. C. to about 200.degree. C., a pressure in the range of from about 1 bar to about 20 bar and during a period of time in the range of from about 20 minutes to about 90 minutes;
- and
- d. cooling the cured wood.
A process for upgrading low-quality wood to high-quality wood comprising the following stages:
- a. softening the low quality wood by directly heating it dielectrically to a temperature in the range of from about 160.degree. C. to about 220.degree. C. for a period of time from about 1 minute to about 2 hours in the presence of an aqueous medium comprising water at a pressure of at least the equilibrium vapor pressure of the aqueous medium at the operating temperature;
- b. drying the softened wood by heating it dielectrically;
- c. curing the dried wood;
- and
- d. cooling the cured wood.