Heat treated stainless steel needles
AssigneeUnited States Surgical Corporation
InventorsSaid Rizk, William O. Powers, W. Scott Samsel
Life of this patent
Estimating the term…
Abstract
Surgical needles are produced from martensitic precipitation-hardening stainless steel and then vacuum heat treated and vacuum cooled to increase its tensile strength while retaining the polished surface of the needle. A needle made by this process is also disclosed.
Claims4
A curved siliconized surgical needle having a diameter of about 11 to about 13 mm, and a taper cut configuration with a needle taper to needle diameter ratio of about 6:1 to about 16:1,
- said needle having a silicon-containing coating and a needle penetration force less than about 35 grams force;
- said needle being curved;
- and
- said needle being made of a stainless steel selected item the group consisting of:
- an alloy comprising about 11 to about 12.5 weight percent chromium, about 7.5 to about 9.5 weight percent nickel, about 0.8 to about 1.4 weight percent titanium, about 0.5 to about 0.6 weight percent molybdenum, about 1.5 to about 2.5 weight percent copper, about 0.04 to about 0.06 weight percent carbon, about 0.4 to about 0.6 percent weight percent manganese, about 0.4 to about 0.6 weight percent silicon, up to about 0.04 weight percent phosphorous, about 0.02 to about 0.04 weight percent sulfur, about 0.1 to about 0.5 weight percent niobium, with the remainder consisting essentially of iron and having about 75 to about 100 g.cm 2 degree offset yield bend moment and
- an alloy comprising about 11.5 to about 12.5 weight percent chromium, about 8.5 to about 9.5 weight percent nickel, about 0.8 to about 1.0 weight percent titanium, about 3.5 to about 4.5 weight percent molybdenum, about 0.5 to about 2.5 weight percent copper, up to about 0.02 weight percent carbon, up to about 0.5 weight percent manganese, up to about 0.5 weight percent silicon, up to about 0.02 weight percent sulfur, with the remainder consisting essentially of iron and having about 100 to about 125 g.cm. 2 degree offset yield bend moment.
A curved siliconized surgical needle having a diameter of 27 to 29 mm, and a taper cut configuration with a needle taper to needle diameter ratio of about 6:1 to about 16:1,
- said needle having a silicon-containing coating and a needle penetration force less than about 200 grams force;
- said needle being curved and having a needle penetration force less than 35 grams force;
- and
- said needle being made of a stainless steel selected from the group consisting of:
- an alloy comprising about 11 to about 12.5 weight percent chromium, about 7.5 to about 9.5 weight percent nickel, about 0.8 to about 1.4 weight percent titanium, about 0.5 to about 0.6 weight percent molybdenum, about 1.5 to about 2.5 weight percent copper, about 0.04 to about 0.06 weight percent carbon, about 0.4 to about 0.6 percent weight percent manganese, about 0.4 to about 0.6 weight percent silicon, up to about 0.04 weight percent phosphorous, about 0.02 to about 0.04 weight percent sulfur, about 0.1 to about 0.5 weight percent niobium, with the remainder consisting essentially of iron and having about 800 to about 1050 g.cm 2 degree offset yield bend moment and
- an alloy comprising about 11.5 to about 12.5 weight percent chromium, about 8.5 to about 9.5 weight percent nickel, about 0.8 to about 1.0 weight percent titanium, about 3.5 to about 4.5 weight percent molybdenum, about 0.5 to about 2.5 weight percent copper, up to about 0.02 weight percent carbon, up to about 0.5 weight percent manganese, up to about 0.5 weight percent silicon, up to about 0.02 weight percent sulfur, with the remainder consisting essentially of iron and having about 1100 to about 1350 g.cm. 2 degree offset yield bend moment.