US 5,527,946 AGranted

Preparation of aliphatic alpha, omega-aminonitriles

AssigneeBASF SE

InventorsKlemens Flick, Johann-Peter Melder, Werner Schnurr, Klaus Ebel, Tom Witzel, Wolfgang Harder, Alwin Rehfinger, Rolf Fischer

Life of this patent

Estimating the term…

patentgrep

Loading patent…

Abstract

Aliphatic alpha, omega-aminonitriles are prepared by partial hydrogenation of aliphatic alpha, omega-dinitriles at elevated temperatures and superatmospheric pressure in the presence of a solvent and of a catalyst by a process which comprises using a catalyst which (a) contains a compound based on a metal selected from the group consisting of nickel, cobalt, iron, ruthenium and rhodium and (b) contains from 0.01 to 25% by weight, based on (a), of a promoter based on a metal selected from the group consisting of palladium, platinum, iridium, osmium, copper, silver, gold, chromium, molybdenum, tungsten, manganese, rhenium, zinc, cadmium, lead, aluminum, tin, phosphorus, arsenic, antimony, bismuth and rare earth metals and (c) from 0 to 5% by weight, based on (a), of a compound based on an alkali metal or on an alkaline earth metal, with the proviso that the component (a) is not based on iron or iron and one of the metals selected from the group consisting of cobalt, ruthenium and rhodium when (b) is a promoter based on a metal selected from the group consisting of titanium, manganese, chromium and molybdenum, and with the further proviso that, when a compound based on only ruthenium or rhodium or ruthenium and rhodium or nickel and rhodium is selected as component (a), the promoter (b) may be dispensed with.

Claims8

Dependent claims

A process for the preparation of aliphatic alpha, omega-aminonitriles of the formula II

NC--(CH.sub.2).sub.n --CH--NH.sub.2 I
where n is an integer from 1 to 10, by partial hydrogenation of aliphatic alpha-omega-dinitriles at elevated temperature and superatmospheric pressure in the presence of a solvent and of a catalyst, which comprises carrying out the partial hydrogenation in the presence of a catalyst which
(a) contains cobalt and
(b) contains from 0.01 to 25% by weight, based on (a), of a promoter based on a metal selected from the group consisting of palladium, platinum, iridium, osmium, iron, copper, silver, gold, chromium, molybdenum, tungsten, manganese, rhenium, zinc, cadmium, lead, aluminum, tin, phosphorus, arsenic, antimony, bismuth and rare earth metals and
(c) from 0 to 5% by weight, based on (a), of a trace component based on a metal selected from the group consisting of an alkali metal and an alkaline earth metal,
said catalyst being obtained by
(I) precipitating precursors of the components (a) to (c) from aqueous solutions in the presence or absence of carriers yielding a precipitate,
(II) optionally processing the resulting precipitate to give extrudates or pellets,
(III) drying the precipitate or pellets or extrudates at a temperature from 80.degree. to 150.degree. C. yielding a dried product, and
(IV) calcining the dried product at a temperature from 150.degree. to 500.degree. C. in a gas stream comprising air or nitrogen yielding a calcined product, then
(V) optionally passivating the surface of the calcined product at from 20.degree. to 80.degree. C. by means of an oxygen/nitrogen mixture yielding a passivated product, then
(VI) activating the calcined or passivated product by exposing it to a reducing atmosphere for from 2 to 24 hours at from 200.degree. to 500.degree. C.

9 more elements