Process for manufacturing plastic parts

A process for manufacturing thin plastic shells comprising the steps of providing a predetermined charge of material made up of microspheres comprising blended thermoplastic resin and plasticizer with pigment additives that constitute less than 5% by weight of the blend;

• the microspheres having a smooth outer surface appearance at magnifications of 80 X and having an outside diameter in a range of 0.007" to 0.040";
• providing a centrifugal mold;
• placing an amount of the predetermined charge of the microspheres into the centrifugal mold corresponding to a weight of the finished thin plastic shell to be removed from the mold;
• and centrifugally and melt flowing the material into a shape of the thin plastic shell corresponding to the heated mold surface;
• thereafter cooling the centrifugally molded thin plastic shell and removing the thin plastic shell from the mold, wherein the miscrospheres cause the thin plastic shell to be formed with low porosity and a uniform thickness without backside irregularities so as to improve shell weight control.

A process for manufacturing thin plastic shells comprising the steps of providing a predetermined charge of material greater than a weight of the thin plastic shell to be molded and comprised of microspheres including blended thermoplastic resin and pigment additives that constitute less than 5% by weight of the blend and wherein the microspheres have a smooth outer surface appearance at magnifications of 80 X and have an outside diameter in a range of 0.007" to 0.040";

• providing a heated mold;
• placing the charge of microspheres into a powder box;
• joining the powder box to the heated mold;
• rotating the powder box to fill the heated mold with an amount of the predetermined charge of the material that imposes a static head on the material that rests on a heated casting surface of the mold;
• melt flowing the material across the heated casting surface into a shape of the thin plastic shell corresponding to the heated casting surface;
• removing excess material;
• and thereafter cooling and removing the finished thin plastic shell from the mold, wherein the microsphres cause the thin plastic shell to be formed with low porosity and a uniform thickness without backside irregularities so as to improve shell weight control.

A process for manufacturing thin plastic shells comprising the steps of providing a predetermined charge of material made up of microspheres having a smooth uniform diameter in a range of 0.007" to 0.040" and comprising blended thermoplastic resin and plasticizer with pigment additives that constitute less than 5% by weight of the blend and wherein the thin plastic shells are processed from the microspheres by slush molding the microspheres from a charge of the material larger than a weight of the thin plastic shell to be cast in a heated mold;

• providing the heated mold;
• placing the charge of microspheres into a powder box;
• joining the powder box to the heated mold;
• rotating the powder box to fill the mold with the charge of the material, which charge imposes a static head on the material that rests on a heated casting surface of the heated mold;
• melt flowing the material across the heated casting surface into a shape of the thin plastic shell corresponding to the heated casting surface;
• removing excess material;
• and thereafter cooling and removing the finished thin plastic shell from the mold, wherein the microspheres cause the thin plastic shell to be formed with low porosity and a uniform thickness without backside irregularities so as to improve shell weight control.