Dehydration of hydrogels
AssigneeHowmedica, Inc.
InventorQi-Bin Bao
Life of this patent
Estimating the term…
Abstract
Novel prosthetic nuclear implants for insertion into vertebral discs are prepared by dehydrating hydrated bulky hydrogel discs under specific conditions so as to reduce the water content as low as possible (down to about 10% by weight) but without distortion of the implants, without the formation of concavities and sharp edges, and without changing the shape of the hydrated implant.
Claims9
A method of dehydrating a bulky hydrogel nuclear vertebral implant having a weight before dehydration between about 3 and about 10 grams and having a shape substantially similar to a human vertebral disc nucleus and having a water content before dehydration between about 30 and about 60% by weight, said method comprising:
- dehydrating said implant at (a) a relative humidity of at least about 80%, (b) at a drying temperature between about 10.degree. and about 40.degree. C., and (c) for a time of drying of more than two days.
A method of dehydration of a hydrated bulky hydrogel implant having an original shape, said hydrogel being highly hydrolyzed polyvinyl alcohol, so as to maintain said original shape of said hydrated implant, said method comprising:
- dehydrating said implant when the water content of said implant is within a range from about 30 to about 60 percent by weight under controlled conditions of relative humidity and temperature and time, wherein said relative humidity is at least about 80%, said drying temperature is within a range from about 10.degree. to about 40.degree. C., and said time of drying is at least two days and sufficient to enable said implant to be dried without distortion to a water content below about 30%, and said implant weighing between about 3 and about 10 grams and having a shape which is substantially similar to a human vertebral disc nucleus.
A method of producing a synthetic vertebral disc implant comprising highly hydrolyzed polyvinyl alcohol having a water content below about 30 weight percent and exhibiting (when viewed with no additional magnification beyond a naked eye) no visible distortion and no sharp edges, and having a minimum dehydrated volume, said method comprising:
- when said implant has a water content between about 30 to about 60 percent by weight, dehydrating said implant at a relative humidity of at least about 80%, at a drying temperature within a range from about 10.degree. to about 40.degree. C., and for a drying time which is at least two days.
Dependencies are inferred from the claim text.