Fire extinguishing and protection agent
OwnerJurgen Buil, Gernot Lohnertinventors
Life of this patent
Estimating the term…
Abstract
The invention concerns the production and use of thickened synthetic amorphous silica in water as a fire extinguishing and protection agent in which the water is mixed with 1% to 9% by weight of fumed silica, and the resulting thin fluid suspension is rapidly thickened with mixing and shearing by the addition of from 0.003% to about 0.5% by weight of an additive selected from the group consisting of polyethylene glycols, polypropylene glycols, and their derivatives thereof, wherein the additive has a molar mass between 700 and 600,000.
Claims12
A composition forming a thickened aqueous fire extinguishing suspension, said composition consisting essentially of:
- (a) fumed silica;
- (b) water in sufficient amount to dissolve said silica and form an amorphous, synthetic silica of 1% to 9% by weight in said water;
- (c) a thickening agent of between 0.003% and about 0.5% by weight, said thickening agent selected from the group consisting of polyethylene glycols, polypropylene glycols, both with molar masses between 700 and 600,000, and the derivatives thereof, said thickening agent providing a thickened suspension through irreversible rheopexy, whereby a sprayable, adhesive, thickened suspension is formed;
- and
- (d) optionally, the thickened suspension includes an additional additive to improve the fire extinguishing action, said additive selected from the group consisting of hydrogen carbonates, borates, and ammonium phosphates.
2 more elements
A process for making a thickened aqueous fire extinguishing suspension consisting essentially of the following steps:
- (a) mixing a fumed silica and water to provide a suspension of amorphous, synthetic silica in water, said suspension having between 1% and 9% by weight of synthetic silica;
- (b) adding a thickening agent to said suspension with mixing to form a thickened suspension, said thickened suspension having between 0.003% and about 0.5% by weight of said thickening agent, said thickening agent selected from the group consisting of polyethylene glycols, PG,27 polypropylene glycols, both with molar masses between 700 and 600,000, and the derivatives thereof;
- (c) optionally mixing an additional additive into the thickened suspension to improve the fire extinguishing action, said additive selected from the group consisting of hydrogen carbonates, borates, and ammonium phosphates;
- (d) retaining said thickened suspension in a fire extinguishing container;
- (e) discharging the thickened suspension from the container to generate a shearing action for additional thickening of the thickened suspension, whereby a sprayable, adhesive, thickened suspension is produced for extinguishing fires;
- and
- (f) optionally, the said process further comprises the additional step of stirring or otherwise agitating the thickened suspension to generate a sheering action for additional thickening of the thickened suspension, said stirring to occur before discharging the thickened suspension either before or after retaining the thickened suspension in the fire extinguishing container.
4 more elements
A process for making a thickened aqueous fire extinguishing suspension consisting essentially of the following steps:
- (a) mixing a fumed silica and a thickening agent, said thickening agent selected from the group consisting of polyethylene glycols, polypropylene glycols, both with molar masses between 700 and 600,000, and the derivatives thereof;
- (b) adding water to said mixture of fumed silica and thickening agent with mixing to create a thickened suspension of amorphous, synthetic silica in water, said thickened suspension having between 1% and 9% by weight of synthetic silica and having between 0.003% and about 0.5% by weight of said thickening agent;
- (c) optionally mixing an additional additive into the thickened suspension to improve the fire extinguishing action, said additive selected from the group consisting of hydrogen carbonates, borates, and ammonium phosphates;
- (d) retaining said thickened suspension in a fire extinguishing container;
- (e) discharging the thickened suspension from the container to generate a shearing action for additional thickening of the thickened suspension, whereby a sprayable, adhesive, thickened suspension is produced for extinguishing fires;
- and
- (f) optionally, the said process further comprises the additional step of stirring or otherwise agitating the thickened suspension to generate a sheering action for additional thickening of the thickened suspension, said stirring to occur before discharging the thickened suspension either before or after retaining the thickened suspension in the fire extinguishing container.
4 more elements
A process for making a thickened aqueous fire extinguishing suspension consisting essentially of the following steps:
- (a) mixing a fumed silica and a thickening agent, said thickening agent selected from the group consisting of polyethylene glycols, polypropylene glycols, both with molar masses between 700 and 600,000, and the derivatives thereof;
- b) retaining said mixture of fumed silica and thickening agent in a dry condition in a first chamber of a fire extinguishing container;
- c) retaining water in a second chamber in the fire extinguishing container;
- and
- d) simultaneously mixing and discharging said water and said mixture of fumed silica and thickening agent to create a thickened suspension of amorphous, synthetic silica in water and to generate shearing action for additional thickening of the thickened suspension, said thickened suspension having between 1% and 9% by weight of synthetic silica and having between 0.003% and about 0.5% by weight of said thickening agent, whereby a sprayable, adhesive, thickened suspension is produced for extinguishing fires.
2 more elements