US 5,512,642 AGranted
Process for making vinyl aromatic/alkoxylated allyl alcohol copolymers
AssigneeArco Chemical Technology, L.P.
InventorShao-Hua Guo
Life of this patent
Estimating the term…
Abstract
An improved process for making vinyl aromatic/allylic alcohol copolymers is disclosed. Gradual addition of a free-radical initiator during the course of the polymerization results in a substantial increase in the polymer yield obtained compared with the yield from conventional processes in which all of the free-radical initiator is charged initially. The process is particularly useful for making commercially important varieties of styrene-allyl alcohol copolymers.
Claims12
A process for making a vinyl aromatic/alkoxylated allyl alcohol copolymer, said process comprising:
- (a) charging a reactor with:
- (i) an alkoxylated allyl alcohol of the formula:
- CH.sub.2 .dbd.CR'--CH.sub.2 --(A).sub.n --OH
- in which R' is selected from the group consisting of hydrogen and methyl, A is a C.sub.2 -C.sub.4 oxyalkylene group, and n, which is the average number of oxyalkylene groups in the alkoxylated allyl alcohol, has a value less than or equal to 5;
- (ii) 10-30% of the total amount to be used of a vinyl aromatic monomer;
- and
- (iii) 45-75% of the total amount to be used of a free-radical initiator;
- (b) heating the reaction mixture at a temperature within the range of about 125.degree. C. to about 185.degree. C.;
- and
- (c) gradually adding to the reaction mixture, at a decreasing rate, the remaining 70-90% of vinyl aromatic monomer and 25-55% of free-radical initiator, to produce a vinyl aromatic/alkoxylated allyl alcohol copolymer having a number average molecular weight within the range of about 800 to about 2000 and a hydroxyl number within the range of about 180 to about 280 mg KOH/g;
- wherein the mole ratio of vinyl aromatic monomer to alkoxylated allyl alcohol used in the process is within the range of about 0.1 to about 0.5, and the yield of copolymer is enhanced as a result of gradual addition of the free-radical initiator.
8 more elements
A process for making a vinyl aromatic/propoxylated allyl alcohol copolymer, said process comprising:
- (a) charging a reactor with:
- (i) a propoxylated allyl alcohol of the formula:
- CH.sub.2 .dbd.CH--CH.sub.2 --(A).sub.n --OH
- in which A is an oxypropylene group, and n, which is the average number of oxypropylene groups in the propoxylated allyl alcohol, has a value less than or equal to 5;
- (ii) 10-30% of the total amount to be used of a vinyl aromatic monomer;
- and
- (iii) 45-75% of the total amount to be used of a free-radical initiator;
- (b) heating the reaction mixture at a temperature within the range of about 125.degree. C. to about 185.degree. C.;
- and
- (c) gradually adding to the reaction mixture, at a decreasing rate, the remaining 70-90% of vinyl aromatic monomer and 25-55% of free-radical initiator, to produce a vinyl aromatic/propoxylated allyl alcohol copolymer having a number average molecular weight within the range of about 800 to about 2000 and a hydroxyl number within the range of about 180 to about 280 mg KOH/g;
- wherein the mole ratio of vinyl aromatic monomer to propoxylated allyl alcohol used in the process is within the range of about 0.1 to about 0.5, and the yield of copolymer is enhanced as a result of gradual addition of the free-radical initiator.
8 more elements
A process for making a styrene/propoxylated allyl alcohol copolymer, said process comprising:
- (a) charging a reactor with:
- (i) a propoxylated allyl alcohol of the formula:
- CH.sub.2 .dbd.CH--CH.sub.2 --(A).sub.n --OH
- in which A is an oxypropylene group, and n, which is the average number of oxypropylene groups in the propoxylated allyl alcohol, has a value within the range of about 1 to 2;
- (ii) 10-30% of the total amount to be used of styrene;
- and
- (iii) 45-75% of the total amount to be used of a free-radical initiator;
- (b) heating the reaction mixture at a temperature within the range of about 125.degree. C. to about 185.degree. C.;
- and
- (c) gradually adding to the reaction mixture, at a decreasing rate, the remaining 70-90% of styrene and 25-55% of free-radical initiator, to produce a styrene/propoxylated allyl alcohol copolymer having a number average molecular weight within the range of about 800 to about 2000 and a hydroxyl number within the range of about 180 to about 280mg KOH/g;
- wherein the mole ratio of styrene to propoxylated allyl alcohol used in the process is within the range of about 0.1 to about 0.5, and the yield of copolymer is enhanced as a result of gradual addition of the free-radical initiator.
8 more elements
Dependencies are inferred from the claim text.