Braze blocking insert for liquid phase brazing operations
AssigneeGeneral Electric Company
InventorsWayne A. Demo, John R. Planchak
Life of this patent
Estimating the term…
Abstract
A preform insert for use in preventing the flow of a braze or solder material into a void in an article during a brazing or soldering operation. The insert is particularly suited to brazing techniques for repairing stator vanes of a gas turbine, though equally effective for use in the manufacture or repair of other articles, as well as soldering operations. The preform insert is composed of a refractory metal oxide powder dispersed in a polymeric solid such that the preform insert is solid yet relatively flexible. As such, the preform insert can be formed to be appropriately shaped and sized to fill a void in an article, such that the void will remain open after the brazing or soldering operation.
Claims9
A method for preventing the flow of a joining material into a void in an article during a joining operation, the method comprising the steps of:
- forming a preform insert comprising a refractory metal oxide powder dispersed in a polymeric solid such that the preform insert is a flexible solid having a shape and size sufficient to fill the void in the article;
- inserting the preform insert in the void in the article such that the preform insert fills the void in the article;
- applying the joining material to a surface of the article;
- heating the article so as to melt and flow the joining material and burn off the polymeric solid so as to leave the refractory oxide in the void, such that the refractory oxide prevents the flow of the joining material into the void during the heating step;
- cooling the article;
- and
- removing the refractory oxide.
A method for preventing the flow of a braze material into a void in an turbomachinery member during a brazing operation, the method comprising the steps of:
- forming a preform insert consisting essentially of an alumina powder dispersed in a thermoplastic polyurethane such that the preform insert is a flexible solid having a shape and size sufficient to fill the void in the turbomachinery member;
- inserting the preform insert in the void in the turbomachinery member such that the preform insert fills the void in the turbomachinery member;
- applying the braze material to a surface of the turbomachinery member;
- heating the turbomachinery member so as to melt and flow the braze material and burn off the thermoplastic polyurethane so as to leave the alumina powder in the void, such that the alumina powder prevents the flow of the braze material into the void during the heating step;
- cooling the turbomachinery member;
- and
- removing the alumina powder from the void.