Floor dry material and method of manufacture
AssigneeCerad Industries, Inc.
InventorHarold J. Manning
Life of this patent
Estimating the term…
Abstract
A floor dry material and method of manufacturing same in which waste cellulosic fibrous material, such as waste paper, is finely shredded after which any metal component is removed and the shredded material is then thoroughly mixed with a biodegradable surfactant, calcium oxide, and water until a temperature about 140.degree. F. to 150.degree. F. is achieved after which a natural citric-based solvent degreaser and a material selected from the group comprising silica diatomite plankton and non-swelling clay are added to obtain a finished floor dry material.
Claims18
A method of manufacturing floor dry material comprising the following steps:
- (1) shredding waste cellulosic fibrous material, to obtain a shredded fiber;
- (2) mixing the shredded fiber of step (1) with a biodegradable surfactant, calcium oxide, and water until a temperature of about 140.degree. F. to 150.degree. F. is achieved to obtain a first mixture slurry;
- (3) mixing a natural citric-based solvent degreaser with the first mixture slurry of step (2) to obtain a second mixture slurry;
- and
- (4) mixing with the second mixture slurry of step (3) a material selected from the group consisting of silica diatomite plankton and non-swelling clay to obtain a finished floor dry material.
A method of manufacturing floor dry material comprising the following steps:
- (1) shredding waste cellulosic fibrous material, to obtain a shredded fiber;
- (2) mixing the shredded fiber of step (1) with a natural citric-based biodegradable surfactant, calcium oxide, and water until a temperature of about 140.degree. F. to 150.degree. F. is achieved to obtain a mixture slurry;
- and
- (3) mixing with the mixture slurry of step (2) a material selected from the group consisting of silica diatomite plankton and non-swelling clay to obtain a finished floor dry material.
A method of manufacturing floor dry material comprising the following steps:
- (1) shredding waste cellulosic fibrous material, to a size of about 500 microns to obtain a shredded fiber;
- (2) passing the shredded fiber from step (1) through a metal separator wherein any metal component in the shredded fiber is removed to obtain a demetalled shredded fiber;
- (3) mixing the demetalled shredded fiber of step (2) with a biodegradable surfactant, calcium oxide, and water at a ratio by weight of the surfactant to the demetalled shredded fiber of about 0.016 to 1, of the calcium oxide to the demetalled shredded fiber of about 0.168 to 1, and of the water to the demetalled shredded fiber of about 2 to 1, until a temperature of about 140.degree. F. to 150.degree. F. is achieved to obtain a first mixture slurry;
- (4) mixing a natural citric-based solvent degreaser with the first mixture slurry of step (3) at a ratio by weight of the solvent degreaser to the demetalled shredded fiber of about 0.01 to 1 to obtain a second mixture slurry;
- and
- (5) mixing with the second mixture slurry of step (4) a material selected from the group consisting of silica diatomite plankton and non-swelling clay at a ratio by weight of the material to the demetalled shredded fiber of about 1 to 1 to obtain a finished floor dry material.
A floor dry material, comprising:
- (a) a waste cellulosic fibrous material;
- (b) a biodegradable surfactant;
- (c) calcium oxide;
- (d) water;
- (e) a natural citric-based solvent degreaser;
- and
- (f) a material selected from the group consisting of silica diatomite plankton and non-swelling clay.
A floor dry material, comprising:
- (a) a waste cellulosic fibrous material, shredded to a size of about 500 microns;
- (b) a biodegradable surfactant at a ratio by weight of the surfactant to the fibrous material of about 0.016 to 1;
- (c) calcium oxide at a ratio by weight of the calcium oxide to the fibrous material of about 0.168 to 1;
- (d) water at a ratio by weight of the water to the fibrous material of about 2 to 1;
- (e) a natural citric-based solvent degreaser at a ratio by weight of the solvent degreaser to the fibrous material of about 0.01 to 1;
- and
- (f) a material selected from the group consisting of silica diatomite plankton and non-swelling clay at a ratio by weight of the material to the fibrous material of about 1 to 1.
Dependencies are inferred from the claim text.