Methods for extending the cycle life of solid, secondary electrolytic cells
OwnerJeremy Barkerinventor
Life of this patent
Estimating the term…
Abstract
Disclosed are methods for extending the cycle life of solid, secondary electrolytic cells employing a solid electrolyte. Also disclosed are solid electrolytes comprising from greater than 80 to about 92 weight percent of electrolytic solvents which, when employed in solid, secondary electrolytic cells extend the cycle life of the cells as compared to solid, secondary electrolytic cells employing solid electrolytes having less solvent.
Claims15
A method for extending the cycle life of a solid, secondary electrolytic cell comprising an anode, a cathode, and a solid, solvent-containing electrolyte, which method comprises:
- (a) preparing a solid electrolyte by curing an electrolytic solution comprising from about 40 to 80 weight percent electrolytic solvent, from about 5 to 30 weight percent of prepolymer, and from about 5 to about 25 weight percent of the alkali salt each based on the total weight of the electrolytic solution;
- (b) incorporating additional electrolytic solvent into the solid electrolyte prepared in (a) above so that the electrolyte comprises solvent in an amount from greater than 80 to less than or equal to about 92 weight percent;
- (c) incorporation the solid electrolyte prepared in (b) above into a secondary electrolytic cell comprising an anode, a cathode and said solid electrolyte interposed therebetween;
- and
- (d) repeatedly charging and discharging the cell.
A method for extending the cycle life of a secondary electrolytic cell comprising an anode, a cathode, and a solid, solvent-containing electrolyte wherein the electrolyte is interposed between the anode and the cathode, which method comprises:
- (a) preparing a cathode/solid electrolyte composite
- wherein the cathode comprises a cyclable cathodic material and from 10 to 50 weight percent of electrolytic solvent, and
- further wherein the solid, solvent-containing electrolyte is derived by curing an electrolyte solution comprising from about 40 to 80 weight percent electrolytic solvent, from about 5 to 30 weight percent of prepolymer, and from about 5 to about 25 weight percent of the alkali salt each based on the total weight of the electrolyte solution;
- (b) applying electrolytic solvent to the surface of said electrolyte of the cathode/solid electrolyte composite prepared in (a) above under conditions wherein the solvent is absorbed into the electrolyte and further wherein sufficient solvent is employed such that, after application, the solid electrolyte comprises electrolytic solvent in an amount from greater than 80 to less than or equal to about 92 weight percent;
- (c) affixing the anode to the surface of the electrolyte of the cathode/electrolyte composite prepared in (b) above;
- and
- (d) repeatedly charging and discharging the cell.
A solid, solvent-containing electrolyte which comprises from about 4 to 10 weight percent of a solid polymeric matrix, from about 4 to about 10 weight percent of an alkali salt and an electrolytic solvent in an amount from greater than 80 weight percent to about 92 weight percent, each based on the total weight of the solid electrolyte.
Dependencies are inferred from the claim text.