Porous dielectric material with improved pore surface properties for electronics applications
AssigneeTexas Instruments Incorporated
InventorsChi-Chen Cho, Bruce E. Gnade, Douglas M. Smith
Life of this patent
Estimating the term…
Abstract
This invention provides an improved porous structure for semiconductor devices and a process for making the same. This process may be applied to an existing porous structure 28, which may be deposited, for example, between patterned conductors 24. The process may include baking the structure in a reducing atmosphere, preferably a forming gas, to dehydroxylate the pore surfaces. The process may include baking the structure in a halogen-containing atmosphere to bond halogens to the pore surfaces. It has been found that a porous structure treated in such a manner generally exhibits improved dielectric properties relative to an untreated sample.
Claims8
A method of modifying a porous dielectric on a semiconductor device comprising:
- (a) providing a substrate containing an uncapped porous dielectric layer, said porous dielectric layer having an average pore diameter between 2 and 80 nm;
- and
- (b) heating said substrate to one or more temperatures between 100 and 490 degrees C. in a controlled atmosphere such that at least 70% of hydroxyl groups initially present on the pore surfaces of said porous dielectric are removed from said porous dielectric, whereby one or more dielectric properties of the porous dielectric are improved.
A method of modifying a porous dielectric on a semiconductor device comprising:
- (a) providing a substrate containing an uncapped porous dielectric layer, said porous dielectric layer having an average pore diameter between 2 and 80 nm;
- (b) placing said substrate in an H.sub.2 -containing, substantially oxygen-free atmosphere;
- and
- (c) heating said substrate to a temperature between 300 and 450 degrees C., at approximately atmospheric pressure, such that at least 70% of hydroxyl groups initially present on the pore surfaces of said porous dielectric are removed from said porous dielectric, whereby one or more dielectric properties of the porous dielectric are improved.