Method for increasing the index of refraction of a glassy material

Abstract

In accordance with the invention, the index of refraction of a glassy material is increased by treating the material with hydrogen and applying heat. Specifically, the glass is exposed to hydrogen or deuterium at pressure in the range 14-11,000 p.s.i. and a temperature in the range 21.degree.-150.degree. C. for a time sufficient for the hydrogen to diffuse into the glass. The glass is then subjected to heat in excess of about 500.degree. C., as by application of a flame or infrared radiation. The duration of heating can be less than a second. The result is a substantial and long-lived increase in the normalized refractive index. For example, flame heating of H.sub.2 loaded commercial GeO.sub.2 doped optical fibers (AT&T Accutether single mode fiber) has produced normalized index changes .increment.n/n of 4.times.10.sup.-3. This process can be used to make and adjust a variety of optical waveguide devices.