Process for preparing uniformly sized, fine particles of polymer
AssigneeKao Corporation
InventorsAkira Yoshimatsu, Akihiro Kondo, Rikio Tsushima
Life of this patent
Estimating the term…
Abstract
Uniformly sized, fine particles of a polymer are produced by: (1) mixing (B) a nonionic-organic compound being liquid at room temperature, having a solubility in water at 25.degree. C. of 0.01 wt. % or larger and being compatible with (A) an oil-soluble, ethylenically unsaturated monomer, with the monomer (A) in an amount of 0.5 to 300 wt. % based on the monomer (A), (2) then adding the mixture of (A) and (B) to an aqueous dispersion of (C) particles of a seed polymer so as to make the mixture of (A) and (B) absorb onto the paricles (C) and (3) polymerizing the mixture of (A), (B) and (C) in the presence of an oil-soluble initiator for the polymerization to obtain said uniformly sized, fine particles.
Claims6
A process for preparing uniformly sized particles of a polymer, which comprises the steps of:
- (1) mixing (A) an oil-soluble, ethylenically unsaturated monomer with (B) a nonionic non-polymerizable organic compound in an amount of 0.5 to 300 wt. % based on said monomer (A) to form a mixture of (A) and (B);
- said nonionic non-polymerizable organic compound (B) being a liquid at room temperature, being compatible with monomer (A), having a solubility of 0.01 wt. % or greater at 25.degree. C. in water and being more soluble in water than monomer (A);
- (2) dispersing said mixture (A) and (B) in water to form a stable, finely dispersed aqueous emulsion of particles of mixture (A) and (B);
- (3) adding said stable finely dispersed emulsion to an aqueous dispersion of (C) particles of a seed polymer, so as to allow said mixture to absorb onto said particles (C), said seed polymer particles have an average particle size of 0.1 to 20 microns and a standard deviation in particle size distribution of 10 percent or less;
- and
- (4) polymerizing (A) in the presence of (B) and (C) and an oil-soluble initiator to obtain said uniformly sized, polymer particles.
A process for preparing uniformly sized particles of a polymer, which comprises the steps of:
- (1) mixing (A) an oil-soluble, ethylenically unsaturated monomer with (B) a nonionic organic alcohol selected from the group consisting of methyl alcohol, ethyl alcohol, isopropyl alcohol, isoamyl alcohol, and octyl alcohol in an amount of 0.5 to 300 wt. % based on said monomer (A) to form a mixture of (A) and (B);
- said nonionic organic alcohol (B) being a liquid at room temperature, being compatible with monomer (A), having a solubility of 0.01 wt. % or greater at 25.degree. C. in water and being more soluble in water than monomer (A);
- (2) dispersing said mixture (A) and (B) in water to form a stable, finely dispersed aqueous emulsion of particles of mixture (A) and (B);
- (3) adding said stable finely dispersed emulsion to an aqueous dispersion of (C) particles of a seed polymer, so as to allow said mixture to absorb onto said particles (C), said seed polymer particles have an average particle size of 0.1 to 20 microns and a standard deviation in particle size distribution of 10 percent or less;
- and
- (4) polymerizing (A) in the presence of (B) and (C) and an oil-soluble initiator to obtain said uniformly sized, polymer-particles.