Utilization of deinking by-product in building materials
AssigneeTran Industrial Research Inc.
InventorHoc N. Tran
Life of this patent
Estimating the term…
Abstract
Deinking by-product from wastepaper recycling operations and pulp mill clarifier sludge are incorporated into drywall or other gypsum-based building products, such as building blocks. The deinking by-product or pulp mill clarifier sludge is diluted and mixed with stucco (calcium sulfate hemihydrate). The resulting slurry preferably is subjected to an initial dewatering, following the on-set of hardening of the gypsum, and drywall or other building product is formed from the dewatered material. A significant loading of fibrous material in the drywall sheet or other gypsum product is achieved using the procedure, imparting improved flexural strength to the product. The preferred procedure also may be used to incorporate virgin or recycled wood pulp into the building product.
Claims12
A method for the production of a building material, which comprises:
- providing a deinking waste sludge from the deinking of wastepaper in a wastepaper recycling procedure comprising a water dispersion having a consistency of about 25 to about 55 wt. % in which the dispersed phase is about 60 to about 80 wt. % organic material and the balance ash,
- diluting said deinking waste sludge from a wastepaper recycling procedure to a viscosity at which it can be readily stirred and to a consistency of about 5 to about 10 wt. %,
- adding calcium sulfate hemihydrate to said diluted deinking by-product to provide a slurry of calcium sulfate hemihydrate and said diluted deinking by-product having a diluted by-product to calcium sulfate hemihydrate ratio of about 1:1 to about 1:5,
- dewatering said slurry to a paste-like mass having a weight ratio of slurry to calcium sulfate of about 0.5:1 to about 1.6:1 for building product formation, and
- forming a building product from said paste-like mass.
A method for the production of a building material, which comprises:
- providing a deinking waste sludge from the deinking of wastepaper in a wastepaper recycling procedure comprising a water dispersion having a consistency of about 25 to about 55 wt. % in which the dispersed phase is about 60 to about 80 wt. % organic material and the balance ash,
- diluting said deinking water sludge to provide a dilute slurry of consistency of about 5 to about 10 wt. %,
- adding calcium sulfate hemihydrate to said dilute slurry to provide a further slurry having a diluted by-product to calcium sulfate hemihyrate ratio of about 1:1 to about 1:5,
- providing sufficient time from about 2 to about 15 minutes for said further slurry to initiate hardening of said calcium sulfate hemihydrate,
- dewatering said further slurry to a paste-like mass having a weight ratio of further slurry to calcium sulfate of about 0.5:1 to about 1.6:1 for building product formation, and
- forming said building product from said dewatered paste-like mass.
A method for the production of a building product, which comprises:
- forming a deinking waste sludge comprising a dilute slurry of water, fibrous material and particulates having a consistency of about 3 to about 10 wt. % by a deinking process in a wastepaper recycling operation,
- mixing said dilute slurry with calcium sulfate hemihydrate to form a further slurry having a dilute slurry to calcium sulfate hemihydrate ratio of about 1:1 to about 1:5,
- providing sufficient time from about 2 to about 15 minutes for said further slurry to initiate hardening of said calcium sulfate hemihydrate,
- dewatering said further slurry to a paste-like mass having a weight ratio of slurry to calcium sulfate of about 0.5:1 to about 1.6:1 for building product formation, and
- forming said building product from the dewatered paste-like mass.