US 5,492,876 AGranted

Solution process for the preparation of polymers of .alpha.-olefins

AssigneeNovacor Chemicals (International) S.A.

InventorsDaniel J. Gillis, Vaclav G. Zboril, Millard C. Hughson

Life of this patent

Estimating the term…

Loading patent…

Abstract

A solution process, and a catalyst therefor, for the preparation of high molecular weight polymers of alpha-olefins viz. homopolymers of ethylene and copolymers of ethylene and C.sub.3 -C.sub.12 alpha-olefins, is disclosed. The process is operated under solution polymerization conditions at 105.degree.-320.degree. C. The catalyst is obtained from titanium tetrahalides, vanadium oxytrihalides and organoaluminum compounds, in which an admixture of catalyst components is heat-treated at 180.degree.-250.degree. C. and subsequently cooled to a temperature of less than 150.degree. C. Additional vanadium oxytrihalide is then added. The resultant catalyst solution is activated with an aluminum compound. The catalyst has good activity, showing superior activity to catalysts in which additional vanadium oxytrihalide is not added or added at temperatures above 150.degree. C.

Claims6

Dependent claims

A coordination catalyst suitable for the preparation of high molecular weight polymers of alpha-olefins, said catalyst having been obtained by combining a first component prepared by the sequential steps of:

(i) admixing a solution of an organoaluminum compound of the formula
AlR.sub.n X.sub.3-n
wherein R is a phenyl radical or a C.sub.1-4 alkyl radical, X is chlorine or bromine and n is 2 or 3, in inert hydrocarbon solvent with a solution of titanium tetrahalide and vanadium oxytrihalide in inert hydrocarbon solvent at a temperature of less than 30.degree. C. and heating the resultant admixture to a temperature of 180.degree.-250.degree. C. for a period of from 15 seconds to 5 minutes;
(ii) cooling the resultant solution to a temperature of less than 150.degree. C.;
and
(iii) admixing the cooled solution with a solution of vanadium oxytrihalide in inert hydrocarbon solvent so as to increase the amount of vanadium in the cooled solution on an atomic basis of at least 10%, with a solution of an organoaluminum compound selected from the group consisting of:
a) organoaluminum compounds of the formula:
AlR.sub.n X.sub.3-n
wherein R is a phenyl radical or a C.sub.1-4 alkyl radical, X is chlorine or bromine and n is 2 or 3;
b) alkyl aluminum siloxalanes of the formula:
R".sub.3 SiO(R".sub.2 SiO).sub.m AlR".sub.2
wherein R" is a C.sub.1-6 alkyl radical and m is 0 or an integer from 1 to 4;
and
c) an aluminoxane compound of the formula:
R'.sub.2 AlO(R'AlO).sub.m AlR'.sub.2
wherein R' is a C.sub.1-6 alkyl radical and m is 0 or an integer from 1 to 4;
wherein:
(A) in step (i) the atomic ratio of:
aluminum to titanium plus vanadium is in the range of 0.2-3.0:1;
and vanadium to titanium is in the range of 0.05:1 to 1.5:1;
and
(B) in the coordination catalyst the atomic ratio of:
aluminum to titanium plus vanadium is in the range of 0.8-7.0:1;
and vanadium to titanium is in the range 0.15-4.0:1.