Hydrogen purification
AssigneeSaes Getters S.P.A.
InventorsMarco Succi, Carolina Solcia, D'Arcy Lorimer
Life of this patent
Estimating the term…
Abstract
An improved apparatus and process for the removal of gaseous impurities from an impure gas stream of hydrogen contaminated with carbon monoxide, and with one or more additional impurities such as carbon dioxide, oxygen, nitrogen, water, methane. The impure gas stream is first contacted with elemental nickel in a first reaction zone under nickel-carbonyl forming conditions thereby converting substantially all the carbon monoxide to nickel carbonyl, thereby producing a partially purified gas stream. The partially purified gas stream is then contacted with Ti.sub.2 Ni or certain manganese-containing alloys in a second reaction zone to produce a fully purified gas stream.
Claims34
A process for the removal of gaseous impurities from an impure hydrogen gas stream contaminated with carbon monoxide, and one or more additional impurities selected from the group consisting of carbon dioxide, oxygen, nitrogen, water, methane, and mixtures thereof, thereby producing a purified hydrogen gas stream;
- said process comprising the steps of:
- I. contacting said impure hydrogen gas stream with elemental nickel in a first reaction zone under nickel-carbonyl forming conditions to convert thereby substantially all the carbon monoxide in said impure hydrogen gas stream to nickel carbonyl, producing a partially purified hydrogen gas stream;
- and then
- II. contacting the partially purified hydrogen gas stream with Ti.sub.2 Ni in a second reaction zone under reacting conditions to produce a fully purified hydrogen gas stream.
A process for the removal of gaseous impurities from an impure hydrogen gas stream contaminated with carbon monoxide, and one or more additional impurities selected from the group consisting of carbon dioxide, oxygen, nitrogen, water, methane, and mixtures thereof, thereby producing a purified hydrogen gas stream;
- said process comprising the steps of:
- I. contacting said impure hydrogen gas stream with elemental nickel in a first reaction zone at a pressure of from about 1 bar to about 20 about bar, under nickel-carbonyl forming conditions to convert thereby substantially all the carbon monoxide in said impure hydrogen gas stream to nickel carbonyl, producing a partially purified hydrogen gas stream;
- and then
- II. contacting the partially purified hydrogen gas stream with Ti.sub.2 Ni in a second reaction zone at a pressure of from about 1 bar to about 20 bar at a temperature of from about 400.degree. C. to about 600.degree. C. under reacting conditions to produce a fully purified hydrogen gas stream;
- wherein said elemental nickel is supported on a carrier having a surface area greater than 100 square meters per gram of weight based on the weight of the carrier;
- wherein the carrier is selected from the group consisting of silicate, titanium silicate and silica;
- wherein the second reaction zone is in a housing with uniformly polished inner walls having a roughness expressed in centerline average height less than 0.25 microns;
- wherein the partially purified hydrogen gas stream in Step II has a velocity of from about 0.5 cubic centimeters per minute to about 50 cubic centimeters per minute per gram of Ti.sub.2 Ni when measured at a pressure of 760 mm Hg and a temperature of 20.degree. C.;
- and
- wherein the Ti.sub.2 Ni is in the form of a loose powder having an average particle size of from about 1 micron to about 250 microns.
A process for the removal of gaseous impurities from an impure hydrogen gas stream contaminated with carbon monoxide, and one or more additional impurities selected from the group consisting of carbon dioxide, oxygen, nitrogen, water, methane, and mixtures thereof, thereby producing a purified hydrogen gas stream;
- said process comprising the steps of:
- I. contacting said impure hydrogen gas stream with elemental nickel in a first reaction zone under nickel-carbonyl forming conditions to convert thereby substantially all the carbon monoxide in said impure hydrogen gas stream to nickel carbonyl, producing a partially purified hydrogen gas stream;
- and then
- II. contacting the partially purified hydrogen gas stream with an alloy of Ti, V, Fe, and Mn wherein:
- the weight ratio of Ti:V is from about 1:100 to about 100:1;
- the weight ratio of Ti:Fe is from about 1:100 to about 100:1;
- and
- the weight ratio of Ti:Mn is from about 1:100 to about 100:1;
A process for the removal of gaseous impurities from an impure hydrogen gas stream contaminated with carbon monoxide, and one or more additional impurities selected from the group consisting of carbon dioxide, oxygen, nitrogen, water, methane, and mixtures thereof, thereby producing a purified hydrogen gas stream;
- said process comprising the steps of:
- I. contacting said impure hydrogen gas stream with elemental nickel in a first reaction zone under nickel-carbonyl forming conditions to convert thereby substantially all the carbon monoxide in said impure hydrogen gas stream to nickel carbonyl, producing a partially purified hydrogen gas stream;
- and then
- II. contacting the partially purified hydrogen gas stream having a manganese-containing alloy of Ti, V, Fe, and Mn wherein:
- the weight ratio of Ti:V is from about 1:100 to about 100:1;
- the weight ratio of Ti:Fe is from about 1:100 to about 100:1;
- and
- the weight ratio of Ti:Mn is from about 1:100 to about 100:1;
- wherein the elemental nickel is supported on a carrier having a surface area greater than 100 square meters per gram of weight based on the weight of the carrier;
- wherein the carrier is selected from the group consisting of silicate, titanium silicate and silica;
- wherein the second reaction zone is in a housing with uniformly polished inner walls having a roughness expressed in centerline average height less than 0.25 microns;
- wherein the partially purified hydrogen gas stream in Step II has a velocity of from about 0.5 cubic centimeters per minutes to about 50 cubic centimeters per minute per gram of manganese-containing alloy when measured at a pressure of 760 mm Hg and a temperature of 20+ C.;
- and
- wherein manganese-containing alloy is in the form of a loose powder having an average particle size of from about 1 micron to about 250 microns.