High efficiency, broad bandwidth, volume holographic element for diffraction windows and method of manufacture

A method of manufacturing a diffractive holographic element for a diffractive window comprising the steps of:

• (a) providing an environment having a controllable relative humidity in which to produce said holographic element;
• (b) coating a medium in said environment with a coat of sensitized gelatin to a thickness of between 2 to 4 microns to form a holographic plate;
• (c) maintaining said relative humidity within said environment at greater than 90% during said coating step for a preselected period of time;
• (d) decreasing said relative humidity within said environment to between 25% and 40% and maintaining said 25% to 40% relative humidity for another preselected period of time;
• (e) exposing said holographic plate with a coherent beam of light that is split into a first and a second diverging beam where said first diverging beam forms an angle between 70 and 80 degrees with said holographic plate and a second diverging beam forms an angle between 30 and 50 degree angle with said holographic plate;
• and
• (f) maintaining said environment at approximately 50% to 60% relative humidity for a preselected period of time during said exposing step in order to produce said holographic element.

A holographic diffractive window for redirecting a beam of electromagnetic radiation wherein said holographic window incorporates therein a holographic element, said holographic window being produced by the following method, said method including the steps of:

• (a) providing an environment having a controllable relative humidity in which to produce said holographic element;
• (b) coating a medium in said environment with a coat of sensitized gelatin to a thickness of between 2 to 4 microns to form a holographic plate;
• (c) maintaining said relative humidity within said environment at greater than 90% during said coating step for a preselected period of time;
• (d) decreasing said relative humidity within said environment to between 25% and 40% and maintaining said 25% to 40% relative humidity for another preselected period of time;
• (e) exposing said holographic plate with a coherent beam of light that is split into both a diverging and a collimated beam where said collimated beam forms an angle between 70 and 80 degrees with said holographic plate and said diverging beam forms an angle between 30 and 50 degrees with said holographic plate;
• and
• (f) maintaining said environment at approximately 50% to 60% relative humidity for a preselected period of time during said exposing step in order to produce said holographic element.

An achromatic holographic diffractive window including a plurality of holographic elements, each of said holographic elements capable of continually diffracting solar radiation toward a specific location on a ceiling during the majority of the day, whereat said diffracted light mixes to form white light;

• wherein each of said holographic elements are produced by the following method, said method including the steps of
• (a) providing an environment having a controllable relative humidity in which to produce said holographic element;
• (b) coating a medium in said environment with a coat of sensitized gelatin to a thickness of between 2 to 4 microns to form a holographic plate;
• (c) maintaining said relative humidity within said environment at greater than 90% during said coating step for a preselected period of time;
• (d) decreasing said relative humidity within said environment to between 25% and 40% and maintaining said 25% to 40% relative humidity for another preselected period of time;
• (e) exposing said holographic plate with a coherent beam of light that is split into both a diverging and a collimated beam where said collimated beam forms an angle between 70 and 80 degrees with said holographic plate and said diverging beam forms an angle between 30 and 50 degrees with said holographic plate;
• and
• (f) maintaining said environment at approximately 50% to 60% relative humidity for a preselected period of time during said exposing step in order to produce said holographic element.