Bonding wire for semiconductor element
AssigneeNippon Steel Corporation
InventorsYasuhide Ohno, Yoshio Ohzeki
Life of this patent
Estimating the term…
Abstract
This invention relates to a bonding wire (3) for connecting electrodes of a semiconductor element to outer leads (2). The bonding wire (3) consists of Cu of not less than 1 wt % but less than 5 wt %, and the balance Au and incidental impurities. The bonding wire is superior in rupture strength and bonding strength. Even if the diameter is thinned to about 10 .mu.m, high reliability may be insured for connection.
Claims12
A bonding wire for a semiconductor element, consisting of Cu of not less than 1 weight % but less than 5 weight %, at least one member selected from the group consisting of Ca, Ge, Be, La and In in an amount of 0.0003 to 0.01 weight % in total, and the balance Au, and having a purity of at least 99.9%, and wherein the diameter of the wire is not greater than 15 .mu.m and having a rupture strength not less than 4 grams.
A bonding wire for a semiconductor element, consisting of Cu of not less than 1 weight % but less than 5 weight %, Pt of not less than 1 weight % but less than 5 weight %, and the balance of Au, and having a purity of at least 99.9%, and wherein the diameter of said wire is not greater than 20 .mu.m.
A bonding wire for a semiconductor element, consisting of Cu of not less than 1 weight % but less than 5 weight %, Pt of not less than 1 weight % but less than 5 weight %, and the balance of Au, and having a purity of at least 99.9%, and wherein said wire has a rupture strength of not less than 4 grams.
A bonding wire for a semiconductor element, consisting of Cu of not less than 3 weight % but less than 5 weight %, and the balance Au, and having a purity of at least 99.9%.
A bonding wire for a semiconductor element, consisting of Cu of not less than 1 weight % but less than 5 weight %, Pt of not less than 1 weight % but less than 5 weight %, at least one selected from the group consisting of Ca, Ge, Be, La and In in an amount of 0.0003 to 0.01 weight % in total, and the balance Au, and having a purity of at least 99.9%, and wherein the diameter of the wire is not greater than 20 .mu.m.
A bonding wire for a semiconductor element, consisting of Cu of not less than 1 weight % but less than 5 weight %, Pt of not less than 1 weight % but less than 5 weight %, at least one selected from the group consisting of Ca, Ge, Be, La and In in an amount of 0.0003 to 0.01 weight % in total, and the balance Au, and having a purity of at least 99.9%, and wherein the wire has a rupture strength of not less than 4 grams.
Dependencies are inferred from the claim text.