Ceramic aluminum laminate and thermally conductive adhesive therefor
AssigneeTRW Inc.
InventorsMansheng Wang, Bruce A. Given
Life of this patent
Estimating the term…
Abstract
A 51/2" by 53/4" flat ceramic board is bonded to an aluminum frame which serves as a heat sink. The bonding agent intermediate the board and the frame is thermally conductive and comprises an epoxy containing Master Bond EP21TDCAOHT. The formed laminate or bond is capable of withstanding repeated stresses occurring through thermal cycling in temperatures from -60 degrees centigrade to +125 degrees centigrade and vibration and humidity testing.
Claims12
A method of heat sinking a ceramic circuit board having a surface of an area of ten square inches or greater to an aluminum sheet to form a heat sinked ceramic circuit board assembly capable of withstanding repeated temperature cycling between -60 degrees C. and +125 degrees C. without breaking or permanent deformation, said method comprising the steps of:
- forming an adhesive mixture with said mixture being thermally conductive and having a dielectric constant of at least 3 when measured at 1 MHz, wherein the step of forming the adhesive mixture comprises the steps of:
- mixing one part by weight of a first adhesive comprising an amine functional polybutadiene blend, a liquid epoxy Novolac resin, alumina, and a flow control agent and one part hardener to form a first mixture element;
- mixing one part by weight of a second adhesive and one part catalyst to form a second mixture element, said second mixing element being a medium viscosity, room temperature curing system capable of being rapidly cured at elevated temperatures;
- and
- mixing one part by weight of said first mixture element with one part by weight of said second mixture element to form said adhesive mixture;
- coating said adhesive mixture over at least a portion of said surface of said ceramic circuit board to form a covering layer thereon;
- placing an aluminum sheet in contact with the adhesive coated surface of said ceramic circuit board, said aluminum sheet having a surface geometry and area at least as great as said surface of the ceramic board so as to cover said adhesive coated surface of said ceramic circuit board;
- and
- placing the ceramic circuit board and aluminum sheet in a vacuum to maintain the elements thereof at a predetermined contact pressure and a predetermined temperature and maintaining said ambient conditions for a predetermined time to cure said adhesive mixture and form the heat sinked ceramic circuit board assembly.
A method of heat sinking a ceramic circuit board such that the circuit board is capable of withstanding repeated temperature cycling between -60.degree. C. and 125.degree. C. without breaking or permanent deformation, said method comprising the steps of:
- providing an adhesive mixture, said adhesive mixture including by weight, approximately 17% of a polyamide hardener, approximately 17% of a liquid epoxy Novolac resin, approximately 58% of fused alumina, and approximately 4% of a flow control agent;
- coating the adhesive mixture over a surface of the ceramic circuit board;
- placing the adhesive coated surface of the ceramic circuit board in contact with a surface of a sheet of aluminum, said sheet of aluminum having an area at least as great as the portion of the ceramic board surface coated with the adhesive mixture;
- and
- placing the ceramic circuit board and the sheet of aluminum in a vacuum for a predetermined period of time to maintain the ceramic circuit board and the sheet of aluminum at a predetermined pressure and a predetermined temperature in order to cure the adhesive mixture.
Dependencies are inferred from the claim text.