Metal treatment
AssigneeAlcan International Limited
InventorsWilliam S. Miller, Roger Grimes
Life of this patent
Estimating the term…
Abstract
A method of treating a blank of an aluminium base alloy comprising a combination of heat treatments and cold forming operations to produce a highly recovered semi-fabricated wrought product that is not statically recrystallized and that is inherently non-superplastic and is capable of superplastic deformation only after an initial non-superplastic deformation to achieve dynamic recrystallization.
Claims16
A method of treating a blank of an aluminium base alloy comprising the steps of hot rolling the blank and thereafter applying a combination of heat treatments and cold forming operations to produce a highly recovered semi-fabricated wrought product which is inherently non-superplastic and is capable of superplastic deformation only after an initial non-superplastic deformation to achieve dynamic recrystallization, wherein said combination comprises at least two said cold forming operations separated by an intermediate annealing step, and wherein said cold forming operations of said combination are such, and said heat treatments of said combination entail temperatures, heating rates and times such that application of said combination substantially avoids recrystallization between the commencement of the first cold forming step and completion of the last cold forming step of the combination, each said cold forming step providing a reduction ratio no greater than 43%.
A method of treating a blank of an aluminium base alloy to produce a highly recovered semi-fabricated wrought product that is inherently non-superplastic and is capable of superplastic deformation only after an initial non-superplastic deformation to achieve dynamic recrystallization, the method comprising the sequential steps of:
- (1) hot rolling the blank;
- (2) holding the previously hot worked blank at a temperature between 275.degree. C. and 425.degree. C. for between 1 and 24 hours;
- (3) allowing the blank to cool to a temperature suitable for cold forming;
- (4) cold forming the blank in a first stage providing a reduction ratio no greater than 43%;
- (5) annealing the cold formed blank, so as to avoid recrystallization, at a temperature of between 300.degree. C. and 400.degree. C. for no more than 2 hours using a controlled heat-up rate of between 10.degree. C. and 200.degree. C./hour, and allowing the annealed product to cool, and
- (6) cold forming the blank in a second stage providing a reduction ratio no greater than 43%.
A method of treating a blank of an aluminium base alloy to produce a highly recovered semi-fabricated wrought product, comprising the sequential steps of:
- (1) hot rolling the blank;
- (2) holding the blank at a temperature between 275.degree. C. and 425.degree. C. for between 1 and 24 hours;
- (3) allowing the blank to cool to a temperature suitable for cold forming;
- (4) cold working the blank to provide a reduction ratio of no more than 43% so as to maintain stored energy within said blank at a level below that which would cause recrystallization during subsequent annealing;
- (5) annealing at a low temperature to provide a recovered structure and avoid recrystallization;
- and
- (6) cold working to provide a reduction ratio of no more than 43% so as to maintain stored energy at a level below that which would cause recrystallization during subsequent heating.
Dependencies are inferred from the claim text.