Thallium-calcium-barium-copper-oxide superconductor with silver and method

A method for forming on a substrate a textured polycrystalline film of 1223 phase thallium system oxide superconductor where crystallites of said polycrystalline film are aligned with a C-axis perpendicular to a surface of the substrate, comprising:

• forming a precursor film on the substrate comprising oxides of calcium, barium, and copper in ratios for forming the 1223 phase thallium system oxide superconductor, and silver, in an amount of about 1 to 20 mole percent of total metals in the precursor film;
• and annealing the precursor film at a temperature from 855.degree. to 860.degree. C. for about 10 to 60 minutes in an oxidizing atmosphere saturated with thallous oxide, where the oxidizing atmosphere comprises oxygen and up to 80 percent of an inert gas selected from the group consisting of nitrogen and argon, kith the source of thallous oxide at a temperature from 735.degree. to 750.degree. C., and where the silver causes a liquid phase formation of the precursor film that incorporates thallium into the film in an amount of about 6 to 12 mole percent of total metals in the film, and said silver facilitates the growth of a microstructure of the 1223 phase thallium system oxide superconductor, thereby forming the textured polycrystalline film of 1223 phase thallium system oxide superconductor.

A method for forming a textured film of 1223 phase thallium superconductor comprising:

• depositing on a substrate, a precursor film comprising nitrates of calcium, barium, and copper and an effective amount of silver nitrate;
• heat treating the precursor film in an oxidizing atmosphere to convert the nitrites to oxides thereby forming an oxide film comprising calcium oxide, barium oxide, copper oxide and silver;
• and then heating the oxide film in a thallous oxide saturated oxidizing atmosphere at a temperature between 855.degree. to 860.degree. C., with the source of thallous oxide at a temperature from 735.degree. to 750.degree. C., where the silver causes a liquid phase formation of the oxide film that incorporates thallium into the film in an amount of about 6 to 22 mole percent and said silver facilitates the growth of a microstructure of said film of 1223 phase thallium superconductor where crystallites of said 1223 thallium superconductor film are aligned with a C-axis perpendicular to a surface of the substrate to form the textured 1223 superconductor film.

A method for making textured thallium system 1223 superconductor film which comprises forming a precursor film on a substrate by applying to a surface of the substrate a liquid coating of an aqueous solution containing dissolved salts of calcium, barium, copper, and silver in stochiometric ratio to form the 1223 superconductor film, heating the liquid coated substrate to dry the coating;

• then heat treating the coated substrate in an oxidizing atmosphere to form the precursor film comprising oxides of calcium, barium, and copper, and silver metal;
• and then heating a precursor film in a thallous oxide saturated oxidizing atmosphere at a temperature of 855.degree. to 860.degree. C., with the source of thallous oxide at a temperature from 735.degree. to 750.degree. C. where the silver causes a liquid phase formation of the precursor film that incorporates thallium into the film in an amount of about 6 to 22 mole percent and where the silver facilitates the growth of a well-connected microstructure of the thallium system 1223 superconductor film where crystallites of the thallium system 1223 superconductor film are aligned with a C-axis perpendicular to the surface of the substrate, to form the textured 1223 superconductor film on the surface of the substrate.

An oxide superconductor film on a substrate consisting essentially of 1223 phase according to Tl.sub.x Ca.sub.2 Ba.sub.2 Cu.sub.3 O.sub.8.5+y where x varies form about 0.7 to 1, and y is a fraction of 1 and having a current carrying capacity of exceeding 100,000 amps per square centimeter at a temperature less than or equal to about 20K in a magnetic field of about 10 tesla.