Aluminum alloy fin material for heat-exchanger
AssigneesFurukawa Electric Co., Ltd., Nippondenso Co., Ltd.
InventorsFujio Himuro, Takeyoshi Doko
Life of this patent
Estimating the term…
Abstract
An aluminum alloy fin material for heat-exchanger with excellent thermal conductance and strength after brazing comprising 0.005 to 0.8 wt. % of Si, 0.5 to 1.5 wt. % of Fe, 0.1 to 2.0 wt. % of Ni, and a balance of Al and inevitable impurities is disclosed. The aluminum alloy fin material can additionally contain 0.01 to 0.2 wt. % of Zr and/or at least one element of the group consisting of not more than 2.0 wt. % of Zn, not more than 0.3 wt. % of In, and not more than 0.3 wt. % of Sn.
Claims4
An aluminum alloy fin composition for heat-exchanger subjected to brazing, consisting essentially of 0.005 to 0.8 wt. % of Si, 0.5 to 1.5 wt. % of Fe, 0.1 to 2.0 wt. % of Ni, from about 0.001 to 0.3 wt. % of In and a balance of Al and inevitable impurities;
- wherein if Mg, Cu and/or Mn are present in said aluminum alloy fin composition, said Mg, Cu and/or Mn is each present in an amount less than 0.03 wt. %.
An aluminum alloy fin composition for heat-exchanger subjected to brazing, consisting essentially of 0.005 to 0.8 wt. % of Si, 0.5 to 1.5 wt. % of Fe, 0.1 to 2.0 wt. % of Ni, 0.01 to 0.2 wt % of Zr, and a balance of Al and inevitable impurities;
- wherein if Mg and/or Mn are present in said aluminum alloy fin composition, said Mg and/or Mn is each present in an amount less than 0.03 wt. %.
An aluminum alloy fin composition for heat-exchanger subjected to brazing, consisting essentially of 0.005 to 0.8 wt % of Si;
- 0.5 to 1.5 wt. % of Fe;
- 0.1 to 2.0 wt. % of Ni;
- from about 0.001 to 0.3 wt. % of In;
- and, optionally, at least one element of the group consisting of not more than 2.0 wt. % of Zn, and not more than 0.3 wt. % of Sn;
- and a balance of Al and inevitable impurities;
- wherein if Mg, Cu and/or Mn are present in said aluminum alloy fin composition, said Mg, Cu and/or Mn is each present in an amount less than 0.03 wt. %.
An aluminum alloy fin composition for heat-exchanger subjected to brazing, consisting essentially of 0.005 to 0.8 wt. % of Si;
- 0.5 to 1.5 wt. % of Fe;
- 0.1 to 2.0 wt. % of Ni;
- 0.01 to 0.2 wt. % of Zr;
- at least one element of the group consisting of not more than 2.0 wt. % of Zn, not more than 0.3 wt. % of In, and not more than 0.3 wt. % of Sn;
- and a balance of Al and inevitable impurities;
- wherein if Mg and/or Mn are present in said aluminum alloy fin composition, said Mg and/or Mn is each present in an amount less than 0.03 wt. %.
Dependencies are inferred from the claim text.