A matte film or sheet formed of a polymeric blend comprising,

• 10 to 80% by weight of component (A):
• a propylene polymer or copolymer having a MFR of 1.about.20 g/10 min.,
• 5 to 30% by weigh of component (B):
• an ethylene-.alpha.-(C.sub.3-12 olefin) copolymer satisfying the following conditions (I) to (IV):
• (I) a density of 0.860 to 0.910 g/cm.sup.3 ;
• (II) a maximum peak temperature of not lower than 100.degree. C. as measured by DSC (differential scanning calorimetry);
• (Ill) an insoluble in boiling n-hexane content of not lower than 10% by weight;
• and
• (IV) a MFR of 0.1.about.2 g/10 min.;
• and
• 5 to 85% by weight of component (C):
• at least one component having a MFR of 0.1.about.2.0 g/10 min. which is a polyolefin graft modified resin of at least one grafting monomer selected from the group consisting of
• a) carboxylic acid group-, carboxylic acid ester group- or carboxylic acid anhydride group-containing monomers,
• b) epoxy group-containing monomers,
• c) hydroxyl group-containing monomers,
• d) amino group-containing monomers, and
• e) alkenyl cyclic imino ether derivative monomers, wherein the ratio of component (A) MFR to component (B) MFR is from 5 to 20, the ratio of component (A) MFR to component (C) MFR is from 5 to 30 and the difference in crystalline temperature of component (A) and component (B) and also component (A) and component (C) is not less than 5.degree. C., and wherein said matte film or sheet has a gloss (60.degree.) of not more than 20%.