Superabsorbent polymer having improved absorption rate and absorption under pressure
AssigneeNalco Chemical Company
InventorsScott J. Smith, Eric J. Lind
Life of this patent
Estimating the term…
Abstract
A carboxylic containing superabsorbent polymer having a swell rate of at least 0.3 g./g.sec., a gel strength of about 40,000 to about 150,000 dynes/cm.sup.2, a centrifuge capacity at 30 minutes of about 20 to about 50 g/g, an absorption permeability under pressure at 60 minutes of at least 5 g/g at wherein the ratio of the absorption permeability under pressure at 15 minutes is at least 25% of the absorption permeability under pressure at 60 minutes is disclosed. The superabsorbent polymer is prepared from a solution of carboxylic containing monomers, a cross linking agent, and a blowing agent. The polymer is subsequently treated with a surface crosslinking agent.
Claims1
A carboxylic containing superabsorbent polymer having a swell rate of from about 0.4 to about 1.5 g./g.sec., a gel strength of from about 50,000 to about 124,000 dynes/cm.sup.2, a centrifuge capacity of about 25 to about 45 g/g, an absorption permeability under pressure at 60 minutes of at least 15 g/g wherein the ratio of the absorption permeability under pressure at 15 minutes is at least 40% of the absorption permeability under pressure at 60 minutes said polymer having been prepared by the steps of:
- A. polymerizing a solution containing vinyl carboxylic acid monomers or water soluble salts thereof and from 0.005 to 2.0 percent by weight of the monomers of a crosslinking agent in the presence of a polymerization initiator having added a carbonate blowing agent immediately before, immediately after, or simultaneously with the initiation of polymerization to form a microcellular hydrogel;
- B. chopping or grinding the microcellular hydrogel into gel pieces having a particle diameter of from about 0.1 mm to about 5.0 cm;
- C. drying the gel pieces at temperatures ranging from about 85 C. to about 210 C.;
- D. grinding the pieces to form a polymer having a particle size of from about 0.05 mm to about 5.0 mm;
- E. mixing 100 parts by weight of the polymer with about 0.001 to about 30 parts by weight of a surface crosslinking agent;
- and,
- F. reacting the polymer with the surface crosslinking agent to crosslink molecular chains existing on a surface of the polymer, forming the superabsorbent polymer.
Dependencies are inferred from the claim text.