Process for making an improved tantalum powder and high capacitance low leakage electrode made therefrom
AssigneeCabot Corporation
InventorHongju Chang
Life of this patent
Estimating the term…
Abstract
A process for producing capacitor grade powder, electrodes, and finished capacitors therefrom having reduced electrical leakage characteristics. The powder is prepared by reacting Group V-B base materials with quantities of between 500 to 7000 ppm of nitrogen and 700 to 3000 ppm of oxygen. Electrical leakage is reduced by at least 28% for electrodes anodized at 100 volts or greater in comparison with electrodes and finished capacitors made from undoped materials. A range of specific charge of up to 25,000 uFV/g is achieved for sintering temperatures of 1400.degree. C. to 1800.degree. C.
Claims38
A process for making low leakage capacitors from a base material containing at least one metal powder selected from Group V-B, comprising:
- reacting a quantity of nitrogen with said base material to form at least 500 to 7000 ppm by weight of nitrogen in said material,
- reacting a quantity of oxygen with said base material sufficient to form at least 700 to 3000 ppm by weight of oxygen in said material,
- forming pellets from said base material and sintering said pellets at temperatures between 1400.degree. C. to 1800.degree. C.,
- subjecting said sintered pellets to anodization voltages of 100 volts or greater,
- forming capacitors from said anodized pellets, and detecting a specific charge of up to about 25,000 uFV/g and improved electrical leakage characteristics.
A process making low leakage capacitors from a base material containing at least tantalum metal powder comprising:
- subjecting said material to a temperature of between about 1200.degree. C. and 1600.degree. C. and forming agglomerates of said material,
- reacting a quantity of nitrogen with said agglomerated material sufficient to form between 1400 to 4400 ppm by weight of nitrogen in said material,
- reacting a quantity of oxygen with said agglomerated material sufficient to form between at least 700 to 3000 ppm by weight of oxygen in said material,
- reacting a quantity of a reducing metal with oxygen present in said reacted material and forming a quantity of metal oxide,
- controlling said quantity of metal oxide to a level of between about 950 ppm to 2900 ppm by weight of oxygen in said material,
- forming pellets from said reacted material and sintering said pellets at temperatures between about 1400.degree. C. to 1800.degree. C., subjecting said sintered pellets to anodization voltages of between 150 and 400 volts, and
- forming capacitors from said anodized pellets having a specific charge of between about 5,100 to about 18,000 uFV/g and electrical leakage which is reduced by greater than 36% with respect to capacitors prepared from said base material.
A process for making low leakage capacitors from a base material containing at least tantalum metal powder comprising:
- subjecting said material to a temperature of between about 1400.degree. C. and 1500.degree. C. and forming agglomerates of said base material,
- reducing said agglomerates to a powder having a screen size of -40 mesh,
- reacting a quantity of magnesium nitride and a quantity of magnesium metal with said powder and forming 1850 to 2550 ppm by weight of nitrogen in said powder,
- reacting said magnesium metal with oxygen in said powder to form a magnesium oxide component,
- removing said oxide to a level of between about 2050 to about 2900 ppm by weight of oxygen in said powder,
- forming pellets from said deoxygenated powder and sintering said pellets at temperatures between about 1550.degree. C. to 1650.degree. C.,
- subjecting said sintered pellets to anodization voltages of between 150 and 200 volts, and
- forming electrodes from said anodized pellets having a specific charge of between about 9,800 to about 15,300 uFV/g and electrical leakage which is reduced by between about 75% to 84% with respect to capacitors prepared from said base material.
A tantalum powder for the manufacture of solid capacitors having high specific charge and low electrical leakage characteristics comprising:
- a BET of less than about 0.6 m.sup.2 /g,
- an average agglomerated particle size of -40 mesh,
- a quantity of nitrogen in the range of about 500 ppm to 7000 ppm by weight nitrogen, and
- a quantity of oxygen in the range of about 700 ppm to 3000 ppm by weight of oxygen.
A capacitor having low electrical leakage characteristics comprising:
- a sintered anode produced from tantalum base material, pressed into a pellet, and sintered at temperatures between 1400.degree. C. and 1800.degree. C.,
- said base material having between 500 to 7000 ppm by weight of nitrogen and between 700 to 3000 ppm by weight of oxygen,
- a layer of anodic tantalum pentoxide formed on the surface of said sintered anode,
- a layer of manganese dioxide adjacent to said tantalum pentoxide,
- a layer of graphite positioned adjacent said manganese dioxide layer,
- an exterior shell in electrical contact with said graphite layer, and
- conductive contacts fixed to said shell.