AssigneesAgency of Industrial Science and Technology, Ministry of International Trade & Industry
InventorsMasaki Yasuoka, Kiyoshi Hirao, Shuzo Kanzaki
Estimating the term…
A sintered ceramic article formed mainly of alumina, having a chemical composition of from 1 to 10% by weight of La.sub.2 O.sub.3, from 0.01 to 0.1% by weight of SiO.sub.2, and the balance of Al.sub.2 O.sub.3 and containing these components in the form of corundum (.alpha.-Al.sub.2 O.sub.3) and lanthanum .beta.-alumina (La.sub.2 O.sub.3.llAl.sub.2 O.sub.3) and a method for the production of a sintered ceramic article formed mainly of alumina, comprising the steps of shaping a mixture of Al.sub.2 O.sub.3, La.sub.2 O.sub.3, and SiO.sub.2, calcining the shaped mixture in the air at a temperature in the range of from 600.degree. C. to 1000.degree. C., and further firing the calcined shaped mixture to a temperature in the range of from 1400.degree. C. to 1800.degree. C.
A sintered ceramic article formed mainly of alumina, having a chemical composition of from 1 to 10% by weight of La.sub.2 O.sub.3, from 0.01 to 0.1% by weight of SiO.sub.2, and the balance of Al.sub.2 O.sub.3, and substantially comprising corundum (.alpha.-Al.sub.2 O.sub.3) and lanthanum .beta.-alumina (La.sub.2 O.sub.3.Al.sub.2 O.sub.3).
A method for the production of a sintered ceramic article formed mainly of the alumina, which comprises shaping a mixture of Al.sub.2 O.sub.3, La.sub.2 O.sub.3, and SiO.sub.2, calcining the shaped mixture in the air at a temperature in the range of from 600.degree. C. to 1000.degree. C., and further firing the calcined shaped mixture to a temperature in the range of from 1400.degree. C. to 1800.degree. C.
Dependencies are inferred from the claim text.