Coating composition for lubrication
AssigneesTakata Corporation, Toyota Jidosha Kabushiki Kaisha
InventorsYoshiyuki Hirokawa, Isao Tonomura, Hirohumi Michioka, Yoshio Fuwa
Life of this patent
Estimating the term…
Abstract
A coating composition to be used for lubrication, which comprises a synthetic resin, a solid lubricant and a friction coefficient adjuster.
Claims7
A coating composition for lubrication comprising 20 to 80% by weight of a synthetic resin, said synthetic resin being a member selected from the group consisting of epoxy resins, phenyl resins, amino resins, polyester-alkyd resins, polyurethane resins, vinyl resins, polyamide-imide resins and silicone resins, 20 to 80% by weight of a solid lubricant, said solid lubricant being formed of polytetrafluoroethylene and at least one of boron nitride and molybdenum disulfide, and 5 to 30% by weight of carbon grade carbon fiber prepared by heating acrylic fiber in an inert gas to 1,000.degree.-1,500.degree. C. or heating pitch fiber in an inert gas to 1,000.degree.-1,400.degree. C.
A coating composition for lubrication consisting essentially of,
- 20 to 80% by weight of a synthetic resin, said synthetic resin being at least one member selected from the group consisting of epoxy resins, phenyl resins, amino resins, polyester-alkyd resins, polyurethane resins, vinyl resins, polyamide-imide resins and silicone resins,
- 20 to 80% by weight of a solid lubricant, said solid lubricant consisting essentially of polytetrafluoroethylene, and at least one of molybdenum disulfide and boron nitride, and
- 5 to 30% by weight of carbon grade carbon fiber prepared by heating acrylic fiber in an inert gas to 1,000.degree.-1,500.degree. C. or heating pitch fiber in an inert gas to 1,000.degree.-1,400.degree. C.,
- said composition having abrasion loss less than 7.0 micrometer, said abrasion loss being measured by the step of coating the composition onto a friction plate, preparing a ring member having hardness of HV 460 and a surface roughness of 0.5 uRa, rotating the ring member at 50 r.p.m., pressing the friction plate with the composition onto the rotating ring member at 500 k.g.f. for 200 hours, and measuring thickness of wearing, dynamic friction coefficient of the coating composition being larger than statical friction coefficient thereof to decrease stick slip.
A coating composition for lubrication comprising,
- 20 to 80% by weight of a synthetic resin, said synthetic resin being a mixture of epoxy resin and amino resin mixed in a ratio of 100 parts by weight of epoxy resin and 20 to 100 parts by weight of amino resin,
- 20 to 80% by weight of a solid lubricant, said solid lubricant being formed of polytetrafluoroethylene and at least one of boron nitride and molybdenum disulfide, and
- 5 to 30% by weight of carbon grade carbon fiber, said carbon fiber having a length of 10 micrometer to 1 millimeter and a diameter of 10 to 50 micrometer and prepared by heating acrylic fiber in an inert gas to 1,000.degree.-1,500.degree. C. or heating pitch fiber in an inert gas to 1,000.degree.-1,400.degree. C.,
- said composition having abrasion loss less than 7.0 micrometer, said abrasion loss being measured by the step of coating the composition onto a friction plate, preparing a ring member having hardness of HV 460 and a surface roughness of 0.5 uRa, rotating the ring member at 50 r.p.m., pressing the friction plate with the composition onto the rotating ring member at 500 k.g.f. for 200 hours, and measuring thickness of wearing, dynamic friction coefficient of the composition being larger than statical friction coefficient thereof to decrease stick slip.
Dependencies are inferred from the claim text.