Pultrusion process for long fiber-reinforced nylon composites

A pultrusion processing method of long fiber-reinforced anionic polymerization nylon composites, said process comprising the steps of:

• individually transferring an active caprolactam sodium salt catalyst composition and a polymeric co-catalyst composition into a tubular mixing device with dry nitrogen gas blanketing, continuously mixing at a temperature of 80.degree.-110.degree. C., wherein said active caprolactam sodium salt catalyst composition is obtained by reacting melt caprolactam having a low moisture content of less than 500 ppm, with sodium hydride catalyst, and said polymeric cocatalyst composition is obtained by mixing a polymeric co-catalyst having two NCO end groups with melt caprolactam having a low moisture content of less than 500 ppm to form a nylon reaction mixture;
• feeding the nylon reaction mixture having a viscosity between 10 and 1500 cps into a closed reinforced fiber impregnating tank with dry nitrogen gas blanketing, then impregnating reinforced fiber, which has been dried and preheated with 250.degree. C. hot air, in said nylon reaction mixture;
• immediately pulling into a hot mold whose temperature is between 165.degree. and 215.degree. C. while conducting nylon anionic polymerization and composites processing and forming a finished product of long fiber-reinforced nylon composites;
• wherein the polymeric co-catalyst with NCO end groups is obtained by reacting isophorone diisocyanate with long chain glycol having two OH end groups at the mole ratio of NCO group and OH group in 1.5-2.2, wherein the long chain glycol is one selected from the group consisting of polypropylene oxide long chain polyether glycol with the molecular weight of 400-4,000 (g/mole), polytetramethylene glycol (PTMG) with the molecular weight of 1,000-2,000 (g/mole), polysilicone long chain glycol with the molecular weight of 1,000-3,205 (g/mole) and the moisture of polypropylene oxide glycol and polysilicone glycol.

A pultrusion processing method of long fiber-reinforced anionic polymerization nylon composites, said process comprising the steps of individually transferring an active caprolactam sodium salt catalyst composition and a polymeric co-catalyst composition into a tubular mixing device with dry nitrogen gas blanketing, continuously mixing at a temperature of 80.degree.-110.degree. C., wherein said active caprolactam sodium salt catalyst composition is obtained by reacting melt caprolactam having a low moisture content of less than 500 ppm, with sodium hydride catalyst, and said polymeric cocatalyst composition is obtained by mixing a polymeric co-catalyst having two NCO end groups with melt caprolactam having a low moisture content of less than 500 ppm, to form a nylon reaction mixture;

• feeding the nylon reaction mixture having a viscosity between 10 and 1500 cps into a closed reinforced fiber impregnating tank with dry nitrogen gas blanketing, then impregnating reinforced fiber, which has been dried and preheated with 250.degree. C. hot air, in said nylon reaction mixture;
• immediately pulling into a hot mold whose temperature is between 165.degree. and 215 .degree. C. while conducting nylon anionic polymerization and composites processing and forming a finished product of long fiber-reinforced nylon composites;
• wherein said reinforced long fiber is preheated and dried in fiber preheating and drying device by hot air at 150.degree.-250.degree. C. and the reinforced fiber impregnating tank is combined with the mold after ceramic or polymer heat-insulating liner, which can sustain high temperature operation condition of at least 220.degree. C., is inserted between the end of said impregnating tank and said hot mold, wherein the proper thickness of said heat-insulating liner is 3 m-10 mm and said liner has the effect that makes the temperature at the junction of the end of said impregnating tank and said liner less than 115.degree. C.