Flexible polyurethane foams and process for preparing them
AssigneeEnichem S.p.A.
InventorsGianflavio Lunardon, Dario Stefani
Life of this patent
Estimating the term…
Abstract
Flexible polyurethane foams having densities lower than 25 kg/m.sup.3 and a load bearing capacity, at a 40% compression, higher than 150N, prepared by reacting a modified polyiso=cyanate with a compound containing active end hydrogens and wherein high levels of water are used as foaming agent, without risk of self-ignition.
Claims12
Flexible polyurethane foams having densities lower than 25 kg/m.sup.3 and a bearing capacity higher than 150N according to standard ISO 2439 at 40% of compression, prepared by reacting, in the presence of carbon dioxide formed in situ and according to the free expansion technique, a modified polyisocyanate and a compound containing active end hydrogens, in which the modified polyisocyanate has a free NCO group content ranging from 10 to 45% by weight, and is obtained from the partial polymerization of an organic polyisocyanate having an isocyanic functionality of at least 2, with at least one polyether polyol having a molecular weight ranging from 500 to 8,000, having a hydroxyl functionality from 2 to 4, and in which the compound which contains active end hydrogens comprises at least one polyether polyol obtained from the condensation of propylene oxide and ethylene oxide, with an ethylene oxide content lower than 50% by weight, and having:
- a) a hydroxyl functionality ranging from 2 to 4;
- b) an equivalent weight ranging from 500 to 2,500 per end hydroxyl group;
- on condition that, when the polyether polyol of the compound containing active end hydrogens has an ethylene oxide content ranging from 0 to 10% by weight, its equivalent weight ranges from 500 to 2,500, while when its ethylene oxide content ranges from 10 to 50% by weight, its equivalent weight ranges from 1,000 to 1,500.
A process for preparing polyurethane foams having densities lower than 25 kg/m.sup.3 and a bearing capacity higher than 150N according to the free expansion technique, which comprises:
- a) reacting a polyisocyanate of general formula (I):
- OCN--R--NCO (I)
- or general formula (II):
- ##STR3## where n is one or more, with at least one polyether polyol having a molecular weight from 500 to 8,000, and a hydroxyl functionality from 2 to 4, to obtain a modified polyisocyanate having a content of free NCO groups ranging from 10 to 45% by weight;
- and
- b) reacting the modified polyisocyanate so obtained with a compound containing active end hydrogens, which comprises at least one polyether polyol obtained from the condensation of propylene oxide and ethylene oxide, with an ethylene oxide content lower than 50% by weight, and having:
- i) a hydroxyl functionality ranging from 2 to 4;
- ii) an equivalent weight ranging from 500 to 2,500 per end hydroxyl group;
- on the condition that, when the polyether polyol of the compound containing active end hydrogens has an ethylene oxide content ranging from 0 to 10% by weight, its equivalent weight ranges from 500 to 2,500, while when its ethylene oxide content ranges from 10 to 50% by weight, its equivalent weight ranges from 1,000 to 1,500, wherein the foaming agent is carbon dioxide generated in situ.
Dependencies are inferred from the claim text.