Ultrafine particles, their production process and their use
AssigneeHitachi, Ltd.
InventorsYoshishige Endo, Takeshi Araya, Masahiko Ono, Takao Kawamura, Hiromitsu Kawamura
Life of this patent
Estimating the term…
Abstract
Ultrafine particles of a composite particulate substance composed of two or more types of inorganic oxides, forming a particle structure in which two or more types of inorganic oxides are mutually mixed or an inorganic oxide of one type is contained in an inorganic oxide of another type, and having an average particle diameter of not more than 0.1 .mu.m, a process for the production of the ultrafine particles, use of the ultrafine particles as a thin film, particularly in an image display face plate and a cathode ray tube, and a process for using the ultrafine particles therefor.
Claims9
A thin film which is composed of ultrafine particles of a composite particulate substance composed of at least two types of inorganic oxides, forming a particulate structure comprising at least an electrically conductive inorganic oxide selected from the group consisting of SnO.sub.2, In.sub.2 O.sub.3 and Sb.sub.2 O.sub.3, and an anti-reflective inorganic oxide comprising SiO.sub.2 and wherein the electrically conductive and the anti-reflective inorganic oxides are mutually mixed or wherein the electrically conductive inorganic oxide is contained in the anti-reflective inorganic oxide, the particulate structure having an average particle diameter of not more than 0.1 .mu.m and a particle size distribution having the following characteristics that:
- a maximum peak is existent in the vicinity of the average particle diameter of the ultrafine particles, an amount of ultrafine particles having a particle diameter in the maximum peak region accounts for not less than 50% based on the total amount, a maximum particle diameter is about two times as large a the average particle diameter, and a minimum particle diameter is about 1/2 thereof,
- and a thickness of said film is 0.1 to 0.2 .mu.m.
An image display face plate having a surface on which a thin film is formed, said thin film being composed of at least two types of inorganic oxides, forming a particulate structure comprising at least an electrically conductive inorganic oxide selected from the group consisting of SnO.sub.2, In.sub.2 O.sub.3 and Sb.sub.2 O.sub.3, and an anti-reflective inorganic oxide comprising SiO.sub.2 and wherein the electrically conductive and the anti-reflective inorganic oxides are mutually mixed or wherein the electrically conductive inorganic oxide is contained in the anti-reflective inorganic oxide, the particulate structure having an average particle diameter of not more than 0.1 .mu.m and a particle size distribution having the following characteristics that:
- a maximum peak is existent in the vicinity of the average particle diameter of the ultrafine particles, an amount of ultrafine particles having a particle diameter in the maximum peak region accounts for not less than 50% based on the total amount, a maximum particle diameter is about two times as large a the average particle diameter, and a minimum particle diameter is about 1/2 thereof,
- and a thickness of said film is 0.1 to 0.2 .mu.m.
A cathode ray tube having a surface on which a thin film is formed, said thin film being composed of at least two types of inorganic oxides, forming a particulate structure comprising at least an electrically conductive inorganic oxide selected from the group consisting of SnO.sub.2, In.sub.2 O.sub.3 and Sb.sub.2 O.sub.3, and an anti-reflective inorganic oxide comprising SiO.sub.2 and wherein the electrically conductive and the anti-reflective inorganic oxides are mutually mixed or wherein the electrically conductive inorganic oxide is contained in the anti-reflective inorganic oxide, the particulate structure having an average particle diameter of not more than 0.1 .mu.m and a particle size distribution having the following characteristics that:
- a maximum peak is existent in the vicinity of the average particle diameter of the ultrafine particles, an amount of ultrafine particles having a particle diameter in the maximum peak region accounts for not less than 50% based on the total amount, a maximum particle diameter is about two times as large a the average particle diameter, and a minimum particle diameter is about 1/2 thereof,
- and a thickness of said film is 0.1 to 0.2 .mu.m.
Ultrafine particles of a composite particulate substance composed of at least two types of particulate substances forming a particulate structure in which at least one electrically conductive inorganic oxide selected from the group consisting of SnO.sub.2, In.sub.2 O.sub.3 and Sb.sub.2 O.sub.3 is contained in an anti-reflective inorganic oxide comprising SiO.sub.2 :
- said particulate structure having an average particle diameter of not more than 0.1 .mu.m.
Dependencies are inferred from the claim text.