Modified microsphere FCC catalysts
AssigneeEngelhard Corporation
InventorsRostam J. Madon, Gerald S. Koermer, John M. Macaoay
Life of this patent
Estimating the term…
Abstract
An in situ process for making improved zeolitic fluid cracking catalyst by spray drying a mixture of hydrous kaolin and spinel, essentially free from metakaolin, calcining the resulting microspheres to convert the hydrous kaolin to metakaolin, and reacting microspheres composed of a mixture of spinel and metakaolin forms of calcined clay with a seeded alkaline sodium silicate solution. The weight percent of hydrous kaolin in the starting (uncalcined) microspheres is greater than the spinel content.
Claims13
A zeolitic fluid catalytic cracking catalyst having reduced coke yield and produced by the steps comprising:
- (a) forming an aqueous slurry containing about 60 to 90 parts by weight hydrated kaolin day and about 40 to 10 parts by weight kaolin day that has been calcined through its characteristic exotherm, and binder;
- (b) spray drying the aqueous slurry to obtain microspheres;
- (c) calcining the microspheres obtained in step (b) at a temperature and for a time sufficient to convert the hydrated kaolin day in the microspheres substantially to metakaolin, but insufficient to cause metakaolin or hydrated kaolin to undergo the characteristic kaolin exotherm and to provide microspheres of calcined day having a ratio of metakaolin to clay calcined through the exotherm in excess of 1:1;
- (d) mixing the microspheres obtained in step (c) with sodium silicate and water to obtain an alkaline slurry;
- (e) heating the slurry of microspheres of calcined clay to a temperature and for a time sufficient to crystallize at least about 40% by weight Y-faujasite in the microspheres, said Y-faujasite being in the sodium form;
- (f) and ion-exchanging the microspheres from step (e) with an ammonium salt solution.
The method for making a high zeolite content fluid catalytic cracking catalyst comprising the steps of
- (a) forming an aqueous slurry containing about 90 to 60 parts by weight hydrated kaolin clay and about 10 to 40 parts by weight kaolin clay that has been calcined through its characteristic exotherm, and sodium silicate binder, said slurry being substantially free from metakaolin;
- (b) spray drying the aqueous slurry to obtain microspheres;
- (e) calcining the microspheres obtained in step (b) at a temperature and for a time sufficient to convert the hydrated kaolin clay in the microspheres substantially to metakaolin, but insufficient to cause metakaolin or hydrated kaolin to undergo the characteristic kaolin exotherm and to provide microspheres of calcined day having total acid solubility between about 23 and 37%;
- (d) mixing the microspheres obtained in step (c) with sodium silicate, sodium hydroxide and water to obtain an alkaline slurry;
- (e) heating the slurry of microspheres of calcined clay to a temperature and for a time sufficient to crystallize at least about 40% by weight Y-faujasite in the microspheres, said Y-faujasite being in the sodium form.