US 5,393,570 AGranted

Process for the production of a multicoat coating, aqueous coating compositions, water-thinnable polyacrylate resins and process for the production of water-thinnable polyacrylate resins

AssigneeBASF Lacke + Farben, AG

InventorsStephan Schwarte, Manfred Dangschat, Manfred Reimann, Carlos Westermann

Life of this patent

Estimating the term…

Loading patent…

Abstract

The invention relates to a process for the production of a multicoat coating in which an aqueous transparent topcoat composition containing a polyacrylate resin as binder is employed. The polyacrylate resin can be obtained by adding, either successively or alternately in part amounts, a mixture of a carboxyl-containing ethylenically unsaturated monomer (a1) and a monomer (a2) free from carboxyl groups and a mixture (b) consisting of (meth)acrylic acid esters which are free from carboxyl groups, of hydroxyl-containing ethylenically unsaturated monomers and, if appropriate, of other ethylenically unsaturated monomers to an organic solvent and carrying out a polymerization in the presence of a radical-forming initiator and, at the end of the polymerization, neutralizing the resultant polyacrylate resin and dispersing it in water. The type and amount of (a1), (a2) and (b) are chosen so that the polyacrylate resin has a hydroxyl value of 40 to 200, an acid value of 20 to 100 and a glass transition temperature (T.sub.G) of -40.degree. C. to +60.degree. C.

Claims11

Dependent claims

Process for the production of a multicoat coating on a substrate surface, wherein the process includes the steps of

(1) applying a pigmented basecoat composition to the substrate surface,
(2) forming a polymeric film from the composition applied in stage (1),
(3) applying a transparent aqueous topcoat composition containing a water-thinnable polyacrylate resin as binder and an amino resin as crosslinking agent to the basecoat obtained in this way, and subsequently
(4) baking the basecoat together with the topcoat,
wherein the topcoat composition contains a water-thinnable polyacrylate resin as binder, which resin is obtained by adding, successively,
(I)
(a1) more than 25 to less than 60% by weight of an ethylenically unsaturated monomer which contains at least one carboxyl group per molecule and is copolymerizable with (b1), (b2), (b3) and (a2), or of a mixture of such monomers, together with
(a2) 40-75% by weight of an ethylenically unsaturated monomer which is free from carboxyl groups and is copolymerizable with (b1), (b2), (b3) and (a1), or of a mixture of such monomers, and
a mixture (b), consisting of
(b1) a (meth)acrylic acid ester which is copolymerizable with (b2), (b3), (a1) and (a2) and is essentially free from carboxyl groups, or a mixture of such (meth)acrylic acid esters, and
(b2) an ethylenically unsaturated monomer which is copolymerizable with (b1), (b3), (a1) and (a2), contains at least one hydroxyl group per molecule and is essentially free from carboxyl groups, or a mixture of such monomers, and, if appropriate,
(b3) an ethylenically unsaturated monomer which is copolymerizable with (b1), (b2), (a1) and (a2), is essentially free from carboxyl groups and is different from (b1) and (b2), or a mixture of such monomers,
to an organic solvent or solvent mixture and carrying out a polymerization in the presence of at least one polymerization initiator, the addition of the mixture (b) commencing only when at least 60% by weight of the components (a1) and (a2) have reacted or
by adding the above alternately in part amounts, to an organic solvent or solvent mixture and carrying out the polymerization in the presence of at least one polymerization initiator, the part amounts consisting in each case of at least 10% by weight of the total amount to be used of the component (a1) and (a2) and the mixture (b) and the addition of a part amount commencing only when at least 60% by weight of the preceding part amount has reacted, and
(II)
at the end of the polymerization, neutralizing, at least partially, the resultant polyacrylate resin and dispersing it in water, the sum of the proportions by weight of (a1) and (a2) always being 100% by weight and the type and amount of (b1), (b2), (b3), (a1) and (a2) being chosen so that the polyacrylate resin has a hydroxyl value of 40 to 200, an acid value of 20 to 100, and a glass transition temperature (T.sub.G) of -40.degree. C. to +60.degree. C.

13 more elements

Transparent aqueous topcoat compositions containing a water-thinnable polyacrylate resin as binder and an amino resin as crosslinking agent, wherein the water-thinnable polyacrylate resin is obtained by adding, successively,

(I)
(a1) more than 25 to less than 60% by weight of an ethylenically unsaturated monomer which contains at least one carboxyl group per molecule and is copolymerizable with (b1), (b2), (b3) and (a2), or of a mixture of such monomers, together with
(a2) 40-75% by weight of an ethylenically unsaturated monomer which is free from carboxyl groups and is copolymerizable with (b1), (b2), (b3) and (a1), or of a mixture of such monomers, and
a mixture (b), comprising
(b1) a (meth)acrylic acid ester which is copolymerizable with (b2), (b3), (a1) and (a2) and is essentially free from carboxyl groups, or a mixture of such (meth)acrylic acid esters, and
(b2) an ethylenically unsaturated monomer which is copolymerizable with (b1), (b3), (a1) and (a2), contains at least one hydroxyl group per molecule and is essentially free from carboxyl groups, or a mixture of such monomers, and, if appropriate,
(b3) an ethylenically unsaturated monomer which is copolymerizable with (b1), (b2), (a1) and (a2), is essentially free from carboxyl groups and is different from (b1) and (b2), or a mixture of such monomers,
to an organic solvent or solvent mixture and carrying out a polymerization in the presence of at least one polymerization initiator, the addition of the mixture (b) commencing only when at least 60% by weight of the components (a1) and (a2) have reacted or
by adding the above alternately, in part amounts, to an organic solvent or solvent mixture and carrying out the polymerization in the presence of at least one polymerization initiator, the part amounts consisting in each case of at least 10% by weight of the total amount to be used of the component (a1) and (a2) and the mixture (b) and the addition of a part amount commencing only when at east 60% by weight of the preceding part amount has reacted, and
(II) at the end of the polymerization, neutralizing, at least partially, the resultant polyacrylate resin and dispersing it in water, the sum of the proportions by weight of (a1) and (a2) always being 100% by weight and the type and amount of (b1), (b2), (b3), (a1) and (a2) being chosen so that the polyacrylate resin has a hydroxyl value of 40 to 200, an acid value of 20 to 100, and a glass transition temperature (T.sub.G) of -40.degree. C. to +60.degree. C.

7 more elements

Water-thinnable polyacrylate resins which are obtained by adding, successively,

(I)
(a1) more than 25 to less than 60% by weight of an ethylenically unsaturated monomer which contains at least one carboxyl group per molecule and is copolymerizable with (b1), (b2), (b3) and (a2), or of a mixture of such monomers, together with
(a2) 40-75% by weight of an ethylenically unsaturated monomer which is free from carboxyl groups and is copolymerizable with (b1), (b2), (b3) and (a1), or of a mixture of such monomers, and
a mixture (b), comprising
(b1) a (meth)acrylic acid ester which is copolymerizable with (b2), (b3), (a1) and (a2) and is essentially free from carboxyl groups, or a mixture of such (meth)acrylic acid esters, and
(b2) an ethylenically unsaturated monomer which is copolymerizable with (b1), (b3), (a1) and (a2), contains at least one hydroxyl group per molecule and is essentially free from carboxyl groups, or a mixture of such monomers, and, if appropriate,
(b3) an ethylenically unsaturated monomer which is copolymerizable with (b1), (b2), (a1) and (a2), is essentially free from carboxyl groups and is different from (b1) and (b2), or a mixture of such monomers,
to an organic solvent or solvent mixture and carrying out a polymerization in the presence of at least one polymerization initiator, the addition of the mixture (b) commencing only when at least 60% by weight of the components (a1) and (a2) have reacted or
by adding the above alternately, in part amounts, to an organic solvent or solvent mixture and carrying out the polymerization in the presence of at least one polymerization initiator, the part amounts consisting in each case of at least 10% by weight of the total amount to be used of the component (a1) and (a2) and the mixture (b) and the addition of a part amount commencing only when at least 60% by weight of the preceding part amount has reacted, and
(II)
at the end of the polymerization, neutralizing, at least partially, the resultant polyacrylate resin and dispersing it in water, the sum of the proportions by weight of (a1) and (a2) always being 100% by weight and the type and amount of (b1), (b2), (b3), (a1) and (a2) being chosen so that the polyacrylate resin has a hydroxyl value of 40 to 200, an acid value of 20 to 100, and a glass transition temperature (T.sub.G) of -40.degree. C. to +60.degree. C.

8 more elements

A process for the preparation of water-thinnable polyacrylate resins, which comprises adding successively

(I)
(a1) more than 25 to less than 60% by weight of an ethylenically unsaturated monomer which contains at least one carboxyl group per molecule and is copolymerizable with (b1), (b2), (b3) and (a2), or of a mixture of such monomers, together with
(a2) 40-75% by weight of an ethylenically unsaturated monomer which is free from carboxyl groups and is copolymerizable with (b1), (b2), (b3) and (a1), or of a mixture of such monomers, and
a mixture (b), comprising
(b1) a (meth)acrylic acid ester which is copolymerizable with (b2), (b3), (a1) and (a2) and is essentially free from carboxyl groups, or a mixture of such (meth)acrylic acid esters, and
(b2) an ethylenically unsaturated monomer which is copolymerizable with (b1), (b3), (a1) and (a2), contains at least one hydroxyl group per molecule and is essentially free from carboxyl groups, or a mixture of such monomers, and, if appropriate,
(b3) an ethylenically unsaturated monomer which is copolymerizable with (b1), (b2), (a1) and (a2), is essentially free from carboxyl groups and is different from (b1) and (b2), or a mixture of such monomers,
to an organic solvent or solvent mixture and carrying out a polymerization in the presence of at least one polymerization initiator, the addition of the mixture (b) commencing only when at least 60% by weight of the components (a1) and (a2) have reacted or
by adding the above alternately, in part amounts, to an organic solvent or solvent mixture and carrying out the polymerization in the presence of at least one polymerization initiator, the part amounts consisting in each case of at least 10% by weight of the total amount to be used of the component (a1) and (a2) and the mixture (b) and the addition of a part amount commencing only when at east 60% by weight of the preceding part amount has reacted, and
(II)
at the end of the polymerization, neutralizing, at least partially, the resultant polyacrylate resin and dispersing it in water, the sum of the proportions by weight of (a1) and (a2) always being 100% by weight and the type and amount of (b1), (b2), (b3), (a1) and (a2) being chosen so that the polyacrylate resin has a hydroxyl value of 40 to 200, an acid value of 20 to 100, and a glass transition temperature (T.sub.G) of -40.degree. C. to +60.degree. C.

8 more elements