US 5,393,405 A · Method of electroforming a gold jewelry article

Abstract

A method of electroforming gold jewelry articles utilizes a first gold/silver electroforming bath which is effective for depositing a relatively soft, ductile gold alloy, and a second gold/silver electroforming bath which is effective for depositing a hard, brittle gold alloy. Prior to the electroforming steps, the method includes the preliminary steps of forming a wax mandrel in a desired configuration, inserting a copper wire into the mandrel and applying a conductive lacquer onto the mandrel. The electroforming method includes the steps of alternately immersing the mandrel into the first and second electroforming baths and electroforming alternating layers of the soft and hard gold alloys over each other to form a laminated gold shell. After the last layer has been electroformed, the wax mandrel is melted and removed from the laminated gold shell thereby forming a hollow jewelry article. The alternating soft and hard layers cooperate to relieve internal stresses within the metal and thereby form a very strong and resilient metal shell. Since the laminated structure of the shell is stronger than a conventional electroformed shell, the thickness of the laminated gold shell can be reduced, and therefore the finished article can be made less expensively than a conventional gold shell.

Claims5

Dependent claims

A method of forming an electroformed gold jewelry article comprising the steps of:

immersing a conductive mandrel in a first electroforming bath which is effective for depositing a first gold alloy having a Vickers hardness between approximately 100 and 175, and electroforming a layer of said first gold alloy onto said mandrel in a predetermined thickness;
and
immersing said mandrel in a second electroforming bath which is effective for depositing a second gold alloy having a Vickers hardness between approximately 200 and 275, and electroforming a layer of said second gold alloy onto said mandrel in a predetermined thickness.

A method of forming an electroformed gold jewelry article utilizing a first gold and silver electroforming bath which is effective for depositing a first gold alloy having a Vickers hardness between approximately 100 and 175, and a second gold and silver electroforming bath which is effective for depositing a second gold alloy having a Vickers hardness between approximately 200 and 275, said method comprising the steps of:

immersing a conductive mandrel in said first electroforming bath and electroforming at a current density between approximately 0.6 and 0.8 A/dm.sup.2, and an agitation speed between approximately 36 and 40 RPM a layer of said first gold alloy onto said mandrel in a thickness between approximately 10 .mu.m and 20 .mu.m;
immersing said mandrel in said second electroforming bath and electroforming at a current density of approximately 1.0 A/dm.sup.2, and an agitation speed between approximately 40 and 50 RPM a layer of said second gold alloy onto said mandrel in a thickness between approximately 3 .mu.m and 8 .mu.m;
immersing said mandrel in said first electroforming bath and electroforming at a current density between approximately 1.2 and 1.4 A/dm.sup.2 and an agitation speed between approximately 58 and 64 RPM a layer of said first gold alloy onto said mandrel in a thickness between approximately 10 .mu.m and 20 .mu.m;
immersing said mandrel in said second electroforming bath and electroforming at a current density of approximately 1.0 A/dm.sup.2 and an agitation speed between approximately 40 and 50 RPM a layer of said second gold alloy onto said mandrel in a thickness between approximately 3 .mu.m and 8 .mu.m;
repeating said previous two steps of alternately immersing and electroforming;
and
immersing said mandrel in said first electroforming bath and electroforming at a current density between approximately 1.2 and 1.4 A/dm.sup.2 and an agitation speed between approximately 58 and 64 RPM a layer of said first gold alloy onto said mandrel in a thickness between approximately 25 .mu.m and 55 .mu.m.

4 more elements

Dependencies are inferred from the claim text.

Method of electroforming a gold jewelry article

Life of this patent

Method of electroforming a gold jewelry article

Life of this patent

Abstract

Claims5