AssigneeKrosaki Corporation
InventorsNaoki Furuta, Masakazu Ootsubo, Setsunori Hamaguchi, Isao Watanabe, Yoichi Furuta, Toshihiro Suruga
Estimating the term…
Disclosed herein are a refractory material of high-purity electrofused magnesia clinker having good resistance to corrosion by slag, especially the slag with a high iron content, at high temperatures under an oxidative environment, and a burned or unburned refractory brick made of such refractory material of high corrosion resistance, which is superior in corrosion resistance as well as spalling resistance. The refractory material comprises more than 10 wt. % of electrofused magnesia clinker containing 98.0 to 99.8 wt. % of MgO, less than 0.05 wt. % of SiO.sub.2, and 0.1 to 2.0 wt. % of CaO. It may be in the form of burned or unburned or prepared unshaped refractories.
An electrofused magnesia clinker for a refractory material consisting essentially of 98.0 to 99.8 wt. % of MgO, less than 0.05 wt. % of SiO.sub.2, and 0.1 to 2.0 wt. % of CaO.
A refractory material comprising electrofused magnesia clinker consisting essentially of 98.0 to 99.8 wt. % of MgO, less than 0.05 wt. % of SiO.sub.2, and 0.1 to 2.0 wt. % of CaO.
A refractory material comprising electrofused magnesia clinker and 3-40 wt. % of a carbonaceous material, said electrofused magnesia clinker consisting essentially of 98.0 to 99.8 wt. % of MgO, less than 0.05 wt. % of SiO.sub.2, and 0.1 to 2.0 wt. % of CaO.
An electrofused magnesia clinker for a refractory material said clinker consisting of crystal containing 98.0 to 99.8 wt. % of MgO, less than 0.05 wt. % of SiO.sub.2, and 0.2 to 1.0 wt. % of CaO.
An electrofused magnesia clinker for a refractory material said clinker consisting of crystal containing 98.0 to 99.8 wt. % of MgO, less than 0.05 wt. % of SiO.sub.2, and 0.2 to 2.0 wt. % of CaO.
An electrofused magnesia clinker for a refractory material said clinker consisting of crystal containing 98.0 to 99.8 wt. % of MgO, less than 0.02 wt. % of SiO.sub.2, and 0.2 to 2.0 wt. % of CaO, in which low-silica periclase crystals have lime which separates on their grain boundary.
A refractory material comprising electrofused magnesia clinker consisting of crystals containing 98.0 to 99.8 wt. % of MgO, less than 0.05 wt. % of SiO.sub.2, and 0.2 to 2.0 wt. % of CaO.
A refractory material comprising more than 10 wt. % of electrofused magnesia clinker consisting of crystals containing 98.0 to 99.8 wt. % of MgO, less than 0.05 wt. % of SiO.sub.2, and 0.2 to 1.0 wt. % of CaO.
A refractory material comprising more than 10 wt. % of magnesia clinker consisting of crystals containing 98.0 to 99.8 wt. % of MgO, less than 0.03 wt. % of SiO.sub.2, and 0.1 to 1.0 wt. % of CaO.
A refractory material comprising more than 10 wt. % of electrofused magnesia clinker consisting of crystals containing 98.0 to 99.8 wt. % of MgO, less than 0.02 wt. % of SiO.sub.2, and 0.2 to 2.0 wt. % of CaO, in which low-silica periclase crystals have lime which separates on their grain boundary.
A refractory material comprising more than 10 wt. % of electrofused magnesia clinker and 3-40 wt. % of a carbonaceous material, said electrofused magnesia clinker containing 98.0 to 99.8 wt. % of MgO, less than 0.02 wt. % of SiO.sub.2, and 0.2 to 2.0 wt. % of CaO in which low-silica periclase crystals have lime which separates on their grain boundary.
Dependencies are inferred from the claim text.