Mixed filament yarn of polyester filaments and nylon filaments
AssigneeE. I. Du Pont de Nemours and Company
InventorsRaymond L. Boles, Benjamin H. Knox, James B. Noe
Life of this patent
Estimating the term…
Abstract
Drawing, especially cold-drawing, or hot-drawing, or other heat-treatments, of spin-oriented crystalline polyester filaments, and particularly polyester feed yarns, that have been prepared by spinning at speeds of, e.g., 4 km/min, and have low shrinkage and no natural draw ratio in the conventional sense, provides useful technique for obtaining uniform filaments of desired denier and thereby provides improved flexibility to obtain filaments and yarns mixed with nylon filaments.
Claims1
A mixed filament yarn, suitable for use as a textile yarn, comprised of spin-oriented polyester filaments and of nylon filaments, wherein said spin-oriented polyester filaments are characterized by an intrinsic viscosity (.eta.) about 0.56 to about 0.68, a minimum tenacity at 7% elongation (T.sub.7) of 0.7 g/d, elongation-to-break (E.sub.B) about 60 to about 90%, boil-off shrinkage (S.sub.1) less than about 10%, thermal stability as measured by a (S.sub.2)-value less than about +1%, net shrinkage (S.sub.12) less than about 8%, maximum shrinkage tension (ST) less than about 0.3 gpd, density (.rho.) about 1.35 to about 1.39 g/cm.sup.3, and crystal size (CS) about 55 to about 90 Angstroms and also at least about a value in Angstroms, expressed in relationship to the density (.rho.), of (250.rho.-282.5);
- and wherein said nylon filaments are characterized by relative viscosity (RV) about 40 to about 80, elongation-to-break (E.sub.B) about 60 to about 90%, boil-off shrinkage (S.sub.1) less than about 10%, and dimensional stability as measured by a (.DELTA.L.sub.135-40 C)-value less than 0.
Dependencies are inferred from the claim text.