Nylon flat yarns
AssigneeE. I. Du Pont de Nemours and Company
InventorsRaymond L. Boles, Jr., Lee W. Keene, Benjamin H. Knox, Ralph W. Nugent
Life of this patent
Estimating the term…
Abstract
Flat continuous multifilament nylon apparel yarns suitable for critical dye applications and a process for making such yarns are provided. The process for making the yarns includes spinning nylon polymer with a relative viscosity between about 35 and about 80 and stabilizing to make a feed yarn. The withdrawal speed in spinning is sufficiently high that highly uniform feed yarns are provided. In the process, feed yarn is drawn and subsequently relaxed, preferably in the form of a warp of yarns, so that the resulting drawn yarns have properties suitable for use as flat yarns and have excellent dye uniformity with large molecule acid dyes.
Claims6
A flat multifilament apparel yarn of nylon 66 polyamide polymer, wherein said polymer, having a melting point (T.sub.M) between about 245.degree. C. and about 265.degree. C., is of relative viscosity (RV) between about 50 and about 80 with about 30 to about 70 equivalent NH2-ends per 10.sup.6 grams of polymer, and wherein said multifilament apparel yarn is further characterized by a residual draw ratio (RDR).sub.D between about 1.25 and about 1.55 with an initial modulus greater than about 15 g/d, a boil-off shrinkage (S) between about 3% and about 10%;
- a C.I. Acid Blue 122 dye transition temperature (T.sub.dye) less than about 65.degree. C., a C.I. Acid Blue 40 apparent dye diffusion coefficient (D.sub.A), measured at 25.degree. C., of at least about 20.times.10.sup.-10 cm.sup.2 /sec, and an apparent pore mobility (APM) greater than about [5-0.37.times.10.sup.-4 APV], wherein the apparent pore volume (APV) is greater than about 4.times.10.sup.4 cubic angstroms.
Dependencies are inferred from the claim text.