Silica microspheres, method of improving attrition resistance and use
AssigneeE. I. Du Pont de Nemours and Company
InventorJo-Ann T. Schwartz
Life of this patent
Estimating the term…
Abstract
High-strength, non-agglomerated uniform porous microspheres of silica produced by spray drying a mixture comprising a colloidal silica sol and an additive selected from ammonium citrate or urea; an attrition resistant catalytic composite consisting essentially of metal crystallites such as palladium, platinum-palladium on said silica microsphere and method for preparing the same; and an improved process for making hydrogen peroxide from the direct combination of hydrogen and oxygen in the presence of said attrition resistant catalytic composite.
Claims8
An attrition resistant catalytic composite consisting essentially of metal crystallites dispersed throughout high-strength, non-agglomerated porous silica microspheres having an average diameter in the range of 1.0 to 50 microns and an average pore size of 2 to 20 nm, which are produced by the process of
- (a) mixing an aqueous sol of colloidal silica particles, having a diameter in the range of 5 to 100 nm, with an effective amount of a soluble additive selected from the group consisting of ammonium citrate and urea to inhibit premature formation of an impervious crust;
- (b) spray drying the mixture to form a powder consisting of microspherical silica particles, said particles comprising a conglomerate of the original colloidal silica particles and said additive;
- (c) calcining the spray dried powder to remove volatile components and to sinter the colloidal silica particles within the microspheres without fusing the microspheres into agglomerates;
- (d) preparing an aqueous solution of a metal salt or metal salts;
- (e) slurrying said powder with said solution;
- and
- (f) drying, treating in a hydrogen atmosphere the resulting powder.
An attrition resistant catalytic composite consisting essentially of metal crystallites dispersed throughout high-strength, non-agglomerated porous silica microspheres having an average diameter in the range of 1.0 to 50 microns and an average pore size of 2 to 20 nm, which are produced by the process of:
- (a) preparing an aqueous solution of a metal salt or metal salts;
- (b) dissolving an additive selected from ammonium citrate or urea;
- (c) adding an aqueous sol of colloidal silica particles, having a diameter in the range of 5 to 100 nanometers;
- (d) spray drying the mixture to form a powder consisting of microspherical silica particles, said particles comprising a conglomerate of the original silica particles with metal salts and ammonium citrate or urea distributed throughout;
- and
- (e) calcining to remove volatile components and to sinter the colloidal silica particles within the microspheres without fusing the microspheres into agglomerates.
A process for preparing an attrition resistance catalyst wherein said catalyst is made by spray drying a mixture comprising colloidal silica, an additive selected from ammonium citrate or urea, and platinum salt, palladium salt or mixtures thereof.
Dependencies are inferred from the claim text.