# US 5,352,641 A · Silicon nitride composite sintered body and process for producing same > Agents: this data is available as JSON from the patentgrep API and MCP server — see https://patentgrep.com/llms.txt - Number: US 5,352,641 A - Document ID: US5352641A - Status: Granted - Kind: A - Application number: 07/956,887 - Filed: 1992-12-14 - Granted: 1994-10-04 - Earliest claimed: 1991-08-13 - Assignees: Sumitomo Electric Industries, Ltd. - Inventors: Jin-Joo Matsui; Akira Yamakawa - Web page: https://patentgrep.com/patent/US5352641A ## CPC - C04B 35/584: based on silicon nitride - C04B: LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE {(roofing granules E04D7/005)}; CERAMICS (devitrified glass-ceramics C03C10/00); REFRACTORIES; TREATMENT OF NATURAL STONE ## Abstract A composite silicon nitride sintered body formed of silicon nitride as a matrix and silicon carbide having particle sizes of 5 to 500 nm as a phase dispersed in the sintered body, wherein the total amount of dispersed silicon carbide is 1 to 40% by volume based on the sintered body, the proportion by volume of the silicon carbide dispersed in the silicon nitride particles is 5 to 99% based on the total amount dispersed, the remainder being present only in the grain boundary of the silicon nitride, and a process for producing a silicon nitride composite sintered body which includes the steps of adding a sintering aid to amorphous composite powders as starting materials consisting of silicon, nitrogen and carbon to form a green compact; firing the green compact in a nitrogen atmosphere at 1350.degree. to 1650.degree. C. as the primary sintering; firing the same at 1600.degree. to 1900.degree. C. as the secondary sintering; and firing the same at 1800.degree. to 2200.degree. C. to transfer the silicon carbide precipitated in the particles of silicon nitride to the grain boundaries thereof. ## Claims ### Claim 1 A silicon nitride composite sintered body which comprises silicon nitride as a matrix and silicon carbide particles having of 5 to 500 nm as a phase dispersed in the sintered body, wherein the total amount dispersed of silicon carbide is 1 to 40% by volume based on the sintered body, the proportion by volume of the silicon carbide dispersed in the silicon nitride particles is 5 to 99% based on the total amount dispersed, the remainder being present in the grain boundary of the silicon nitride. ### Claim 2 (depends on 1) The silicon nitride composite sintered body according to claim 1 wherein the proportion by volume of the silicon carbide dispersed in the silicon nitride particles is 35 to 65% based on the total amount of silicon carbide dispersed. ### Claim 3 (depends on 1) The silicon nitride composite sintered body according to claim 1 wherein neither glass phase nor an impurities phase exists int he interfaces between said silicon nitride particles and said silicon carbide particles dispersed in the particles and grain boundaries of the silicon nitride, the interfaces being firmly bonded to each other. ### Claim 4 A composite sintered body of silicon nitride-silicon carbide containing 1 to 30% by volume of silicon carbide as a dispersed phase in the silicon nitride, wherein an amorphous phase of silicon carbide is present in the grain boundaries of silicon nitride and microcrystals of silicon carbide having particle sizes of 5 to 500 nm. are dispersed in said amorphous phase of silicon carbide. ### Claim 5 The composite sintered body of silicon nitride-silicon carbide according to claim (4), wherein the proportion of the amorphous phase of silicon carbide is 20 to 99% by volume based on the total amount dispersed of silicon carbide. ### Claim 6 A process for producing a silicon nitride composite sintered body comprising; adding at least one sintering aid selected from the group consisting of alumina, yttria, magnesia, and aluminum nitride to an amorphous composite powder starting material comprising silicon, nitrogen, and carbon, said sintering aid being present in a total amount of 1 to 15% by weight; to form a green compact, firing, as a primary firing, said green compact in a nitrogen atmosphere by a hot pressing or an atmospheric-pressure sintering process at 1350.degree. to 1650.degree. C. to crystallize said starting material into .alpha.-silicon nitride, and simultaneously effect phase transition to a .beta.-crystal phase; conducting a secondary firing at 1600.degree.0 C. to 1900.degree. C. to allow .alpha.- or .beta.- silicon carbide crystals to precipitate in particles of the silicon nitride; and firing at 1800.degree. C. to 2200.degree. C. to transfer a portion of the silicon carbide crystals precipitated in the particles of the silicon nitride to grain boundaries thereof. ### Claim 7 (depends on 6) The process according to claim 6 wherein amorphous composite powders consisting of silicon, nitrogen and carbon are heat-treated in a nitrogen atmosphere at 1550.degree. to 1700.degree. C. for at least 3 hours and the resultant composite powders consisting mainly of silicon, nitrogen and carbon and having an .alpha.-crystal phase of silicon nitride with a rate of crystallization of 65% or more are employed as the starting material. ### Claim 8 (depends on 7) The process according to claim 7 wherein the carbon content in said amorphous composite powders is 1 to 10% by weight. ### Claim 9 (depends on 6) The process according to claim 6, wherein at least two sintering aids selected from among alumina, yttria, magnesia and aluminum nitride are added in their total amount of 1 to 15% weight. ### Claim 10 (depends on 7) The process according to claim 7 wherein the composite powders having an .alpha.-crystal phase or composite powders having an .alpha.-crystal phase incorporated with sintering aids or the green compact thereof are heat-treated in the air at 400.degree. to 1000.degree. C. for 0.5 to 50 hours to remove residual free carbon through oxidation. ### Claim 11 A process for producing a silicon nitride composite sintered body comprising; adding at least two sintering aids selected from the group consisting of alumina, yttria, magnesia, and aluminum nitride to an amorphous composite powder starting material comprising mixed powders of amorphous silicon nitride and carbon, to form a green compact, in which said sintering aid is present in a total amount of 1% to 15% by weight; firing, as a primary firing, the green compact in a nitrogen atmosphere by a hot pressing or an atmospheric pressure sintering process at 1350.degree. C. to 1650.degree. C. to form a solid solution of carbon and silicon nitride, crystallize said silicon nitride into .alpha.-silicon nitride, and simultaneously effect phase transition to a .beta.-crystal phase; and firing at 1800.degree. C. to 2200.degree. C. to precipitate .alpha.- or .beta.-silicon carbide crystals in particles of the silicon nitride, and to transfer a portion of the silicon carbide crystals precipitated in the particles of silicon nitride to grain boundaries thereof. ### Claim 12 A process for producing a silicon nitride composite sintered body comprising; conducting a primary firing of an amorphous composite powder, comprising amorphous silicon nitride and carbon, in a nitrogen atmosphere by a hot pressing or an atmospheric-pressure sintering process at 1350.degree. to 1600.degree. C., to form a solid solution of carbon and silicon nitride, crystallize said silicon nitride into .alpha.-silicon nitride, and cause a phase transition to a .beta.-crystal phase to form a resulting material; adding to the resulting material at least two sintering aids selected from the group consisting of alumina, yttria, magnesia, and aluminum nitride, in a total amount of 1% to 15% by weight; firing the resulting mixture at a temperature of 1800.degree. C. to 2200.degree. C. to precipitate .alpha.- or .beta.-silicon carbide crystals in the particles of the silicon nitride, and transfer a portion of the silicon carbide crystals precipitated in particles of the silicon nitride to grain boundaries thereof.