# US 5,352,639 A · Tellurium and selenium halide-based glasses, their preparation and use

> Agents: this data is available as JSON from the patentgrep API and MCP server — see https://patentgrep.com/llms.txt

- Number: US 5,352,639 A
- Document ID: US5352639A
- Status: Granted
- Kind: A
- Application number: 07/961,890
- Filed: 1993-03-11
- Granted: 1994-10-04
- Earliest claimed: 1990-07-12
- Assignees: Centre National de la Recherche Scientifique (CNRS)
- Inventors: Jacques Lucas; Xiang H. Zhang
- Web page: https://patentgrep.com/patent/US5352639A

## CPC

- C03C 3/323: {containing halogen, e.g. chalcohalide glasses}
- Y10S 501/904: Infrared transmitting or absorbing
- C03C: CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
- Y10S: TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS

## Abstract

Vitreous solid compositions of formula I: Te.sub.w Se.sub.y X.sub.x Z.sub.z (I) wherein X represents at least one halogen selected from chlorine, bromine and iodine, Z represents at least one element selected from As, Sb and Bi, w, x, y and z represent the molar percentages respectively of elements Te, X, Se and Z, w being a number varying from 5 to 50, x being a number varying from 5 to x.sub.1, y being a number varying from 5 to 80, z being a number varying from 5 to z.sub.1, the numbers w, x, y and z being such that the sum (w+x+y+z) is equal to 100, the numbers x.sub.1 and z.sub.1 being such that: when X represents mostly iodine, x.sub.1 =50 and z.sub.1 =60, when X represents mostly bromine, x.sub.1 =60 and z.sub.1 =50, and when X represents mostly chlorine, x.sub.1 =60 and z.sub.1 =40, it being understood that the molar percentage of Bi, when it is present, is not greater than 12 and that the molar percentage of the element Sb, when it is present, is not greater than 20; their preparation and their use principally in the field of infrared transmission.

## Claims

### Claim 1

Solid vitreous compositions of formula I:
Te.sub.w Se.sub.y X.sub.x Z.sub.z (I)
wherein
X represents at least one halogen selected from chlorine, bromine and iodine,
Z represents at least one element selected from As, Sb and Bi,
w, x, y and z represent the molar percentages respectively of the elements Te, X, Se and Z,
w being a number varying from 10 to 40,
x being a number varying from 5 to x.sub.1,
y being a number varying from 5 to 65,
z being a number varying from 5 to z.sub.1,
the numbers w, x, y and z being such that the sum (w+x+y+z) is equal to 100,
the numbers x.sub.1 and z.sub.1 being such that:
when X represents greater than 50% iodine, x.sub.1 =50 and z.sub.1 =60,
when X represents greater than 50% bromine, x.sub.1 =60 and z.sub.1 =50, and
when X represents greater than 50% chlorine, x.sub.1 =60 and z.sub.1 =40,
it being understood that the molar percentage of Bi, when it is present, is not greater than 12 and that the molar percentage of the element Sb, when it is present, is not greater than 20.

### Claim 2 (depends on 1)

Vitreous compositions according to claim 1, characterized by the fact that X represents iodine, bromine or their mixtures.

### Claim 3 (depends on 1)

Compositions according to claim 1, characterized by the fact that z is a number at least equal to 10.

### Claim 4 (depends on 3)

Compositions according to claim 3, characterized by the fact that w is a number varying from 15 to 25, x from 5 to 15, y from 20 to 60, and z from 10 to 50.

### Claim 5 (depends on 4)

Compositions according to claim 4, characterized by the fact that y can vary from 30 to 50 and/or z from 20 to 40.

### Claim 6 (depends on 4)

Compositions according to claim 4, characterized by the fact that y can vary from 35 to 45 and/or z can vary from 25 to 35.

### Claim 7 (depends on 3)

Compositions according to claim 3, characterized by the fact that w can vary from 10 to 20, x from 5 to 15, y from 55 to 65 and z from 10 to 25.

### Claim 8 (depends on 7)

Compositions according to claim 7, characterized by the fact that w can vary from 10 to 20 and/or z can vary from 10 to 20.

### Claim 9 (depends on 3)

Compositions according to claim 3, characterized by the fact that w can vary from 10 to 20, x from 15 to 25, y from 25 to 35 and z from 30 to 40.

### Claim 10 (depends on 1)

Composition according to claim 1, characterized by the fact that Z represent greater than 50% As.

### Claim 11 (depends on 10)

Compositions according to claim 10, characterized by the fact that Z represents As.

### Claim 12 (depends on 1)

Compositions according to claim 1, characterized by the fact that X represents greater than 50% iodine.

### Claim 13 (depends on 12)

Compositions according to claim 12, characterized by the fact that X represent iodine.

### Claim 14 (depends on 3)

Compositions according to claim 3, characterized by the fact that X represents greater than 50% bromine, w is a number varying from 15 to 25, x from 5 to 15, y from 45 to 55 and z from 15 to 25.

### Claim 15 (depends on 14)

Compositions according to claim 14, characterized by the fact that X represents bromine.

### Claim 16 (depends on 14)

Compositions according to claim 14, characterized by the fact that Z represents greater than 50% As.

### Claim 17 (depends on 1)

Process for preparing vitreous compositions such as defined in claim 1, characterized by the fact that one mixes, in the amounts indicated by formula I, a source of tellurium with a source of halogen, a source of selenium, and a source of the element Z, that one heats the said mixture in an inert atmosphere or under a vacuum to a temperature sufficient to obtain a complete fusion of the starting products, that one maintains the resulting liquid at said temperature for a time sufficient to homogenize the liquid mixture, that, if desired, one puts it into a form, and that one cools it to obtain a vitreous solid.

### Claim 18 (depends on 17)

Process according to claim 17, characterized by the fact that the forming step comprises transferring it in a mold to obtain by moderate pressure a large piece of the desired form.

### Claim 19 (depends on 17)

Process according to claim 17, characterized by the fact that, to obtain a glass preform having a double index, one prepares a glass bar that one places in the center of a cylindrical crucible having an interior diameter greater than the diameter of the bar, the said crucible containing, in the liquid and viscous state, a glass having an index lower than that of said glass bar, and that one lets the whole to cool.

### Claim 20 (depends on 17)

Process according to claim 17, characterized by the fact that, to obtain a glass preform having a double index, one prepares a glass bar that one places at the center of a cylindrical crucible having an interior diameter greater than the diameter of the bar, that one pours into the crucible a second glass having a lower index, in the softened state, so that it fills the space around the bar, and that one lets the whole to cool.