# US 5,352,533 A · Ceramic composite body, process for producing a ceramic composite > Agents: this data is available as JSON from the patentgrep API and MCP server — see https://patentgrep.com/llms.txt - Number: US 5,352,533 A - Document ID: US5352533A - Status: Granted - Kind: A - Application number: 07/946,307 - Filed: 1992-10-26 - Granted: 1994-10-04 - Earliest claimed: 1990-06-01 - Assignees: Krupp Widia GmbH - Inventors: Klaus Dreyer; Dieter Kassel; Hans Kolaska - Web page: https://patentgrep.com/patent/US5352533A ## CPC - C04B 35/6455: {Hot isostatic pressing} - C04B 35/111: Fine ceramics - C04B 35/80: Fibres, filaments, whiskers, platelets, or the like - C04B: LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE {(roofing granules E04D7/005)}; CERAMICS (devitrified glass-ceramics C03C10/00); REFRACTORIES; TREATMENT OF NATURAL STONE ## Abstract A composite body includes 5 to 40% by mass of SiC whiskers and/or up to 80% by mass SiC lamellae and/or of up to 75% by mass SiC powder, 0.05 to 3% by mass of at least one component selected from the group of Y.sub.2 O.sub.3, SiO.sub.3, MgO, NiO and AlN and/or up to 40% by mass of at least one compound selected from the group of carbides, nitrides or carbonitrides of a metal from one of the Groups IVa, Va, Via of the Periodic Table of elements, and/or up to 40% by mass of at least one oxide of at least one metal selected from the group which consists of the metals of Group IVa of the Periodic Table of elements, 0.05 to 10% by mass of a metal constituent selected from the group which consists of at least one element selected from the group including nickel, cobalt and iron, and of the group which consists of chromium in an amount up to 25% of the mass of the metal constituent with the balance being at least one element selected from the group which consists of nickel, cobalt and iron, and a minimum of 30% by mass Al.sub.2 O.sub.3 to the balance of the body. ## Claims ### Claim 1 A fiber-reinforced ceramic composite body consisting of: (a) 5 to 40% by mass of a SiC constituent selected from the group which consists of SiC whiskers, of SiC whiskers and up to 80% by mass SiC lamellae, and of SiC whiskers and up to 2/3 of the total SiC mass as SiC powder; (b) at least one component selected from the group which consists of components (b.sub.1), (b.sub.2) and (b.sub.3) wherein component (b.sub.1) is 0.05 to 3% by mass of at least one compound selected from the group which consists of Y.sub.2 O.sub.3, SiO.sub.3, NgO, NiO and AlN, component (b.sub.2) is up to 40% by mass of at least one compound selected from the group which consists of carbides, nitrides or carbonitrides of a metal from one of the Groups IVa, Va, Via of the periodic Table of elements, and component (b.sub.3) is up to 40% by mass of at least one oxide of at least one metal selected from the group which consists of the metals of Group IVa of the Periodic Table of elements; (c) 0.05 to 10% by mass of a metal constituent selected from the group which consists of at least one element selected from the group which consists of nickel, cobalt, iron and chromium in an amount up to 25% of the mass of the metal constituent with the balance being at least one element selected from the group which consists of nickel, cobalt and iron; and (d) a minimum of 30% by mass Al.sub.2 O.sub.3 to the balance of the body. ### Claim 2 (depends on 1) The composite body defined in claim 1 wherein said at least one element selected from the group which consists of nickel, cobalt and iron is present in an amount of 0.4 to 3% by mass. ### Claim 3 (depends on 1) The composite body defined in claim 1, further comprising up to 2% by mass of an element selected from the group which consists of gold, silver, platinum, iridium, rhodium, ruthenium, palladium and osmium. ### Claim 4 (depends on 1) The composite body defined in claim 1, further comprising up to 20% by mass of at least one compound selected from the group which consists of ZrO.sub.2, HfO.sub.2 and Si.sub.3 N.sub.4. ### Claim 5 (depends on 2) The composite body defined in claim 2 wherein at least one surface coating is applied and includes a group consisting of oxides, carbides, nitrides and carbonitrides of at least one element from the group consisting of group IVa, Va and VIa of the periodic table and Al.sub.2 O.sub.3. ### Claim 6 A process for producing a ceramic composite body of the following ingredients: (a) 5 to 40% by mass of a SiC constituent selected from the group which consists of SiC whiskers, of SiC whiskers and up to 80% by mass SiC lamellae, and of SiC whiskers and up to 75% by mass SiC powder; (b) at least one component selected from the group which consists of components (b.sub.1), (b.sub.2) and (b.sub.3) wherein component (b.sub.1) is 0.05 to 3% by mass of at least one compound selected from the group which consists of Y.sub.2 O.sub.3, SiO.sub.3, MgO, NiO and AlN, component (b.sub.2) is up to 40% by mass of at least one compound selected from the group which consists of carbides, nitrides or carbonitrides of a metal from one of the Groups IVa, Va, Via of the Periodic Table of elements, and component (b.sub.3) is up to 40% by mass of at least one oxide of at least one metal selected from the group which consists of the metals of Group IVa of the Periodic Table of elements; (c) 0.05 to 10% by mass of a metal constituent selected from the group which consists of at least one element selected from the group which consists of nickel, cobalt and iron, and of the group which consists of chromium in an amount up to 25% of the mass of the metal constituent with the balance being at least one element selected from the group which consists of nickel, cobalt and iron; and (d) a minimum of 30% by mass Al.sub.2 O.sub.3 to the balance of the body, said process comprising the steps of: (a) mixing the ingredients of said composite body, preparing thereby an initial powder; (b) wet grinding said powder; (c) thereafter drying and optionally granulating said powder to a dry powder; (d) thereafter pressing said dry powder by uniaxial or isostatic hot pressing, thereby forming a pressed body; (e) sintering said pressed body in a temperature range from 1450.degree. to 1800.degree. C. to produce a sintered body; and (f) immediately thereafter subjecting said sintered body to hot isostatic densification at a pressure range from 5 to 2000 bar. ### Claim 7 (depends on 6) The process defined in claim 6 wherein said steps (e) and (f) are conducted in an atmosphere of inert gas. ### Claim 8 (depends on 7) The process defined in claim 7 wherein said inert gas is argon or nitrogen. ### Claim 9 (depends on 6) The process defined in claim 6 wherein said steps (e) and (f) are conducted in vacuum. ### Claim 10 (depends on 6) The process defined in claim 6 wherein said step (d) is a hot isostatic pressure step. ### Claim 11 (depends on 6) The process defined in claim 6 wherein said step (d) is an uniaxial pressure step. ### Claim 12 (depends on 6) The process defined in claim 6 wherein said step (f) is conducted at a temperature lying below a temperature at which said step (e) is conducted by approximately 100.degree. C. ### Claim 13 (depends on 6) The process defined in claim 6, further comprising a step of uniformly mixing colloidal particles with a crystalline grain size less than 20 nm of gold, silver, platinum, iridium, rhodium, ruthenium, palladium or osmium with said initial powder. ### Claim 14 (depends on 13) The process defined in claim 13 wherein said particles are mixed as colloidal hydrosol or colloidal lyosol in an organic solution. ### Claim 15 (depends on 14) The process defined in claim 14 wherein said organic solution is acetone or i-propanol. ### Claim 16 (depends on 13) The process defined in claim 13 wherein said particles are a colloidal hydrosol or colloidal lyosol in an aqueous solution.