# US 5,350,834 A · Treatment of polyarylene sulfide/sulfone polymers > Agents: this data is available as JSON from the patentgrep API and MCP server — see https://patentgrep.com/llms.txt - Number: US 5,350,834 A - Document ID: US5350834A - Status: Granted - Kind: A - Application number: 08/062,641 - Filed: 1993-05-14 - Granted: 1994-09-27 - Earliest claimed: 1989-11-06 - Assignees: Phillips Petroleum Company - Inventors: Rex L. Bobsein; Michael C. Yu; Roy F. Wright; David A. Soules - Web page: https://patentgrep.com/patent/US5350834A ## CPC - C08G 75/02: Polythioethers - C08G 75/20: Polysulfones - C08G: MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS ## Abstract Poly(arylene sulfide/sulfone) polymers are treated in order to increase melt stability and decrease impurities by contacting the poly(arylene sulfide/sulfone) polymer with a soluble zinc compound and an acidic solution. In one embodiment, the polymer is treated first with the soluble zinc compound, followed by treatment with the acidic solution. In another embodiment, the polymer is treated in one step with a solution comprising a water soluble zinc compound in an acidic solution. ## Claims ### Claim 1 A method of treating a poly(arylene sulfide/sulfone) polymer in order to increase said polymer's thermal stability and purity, which method comprises a) contacting a poly(arylene sulfide/sulfone) polymer at a temperature in the range of 0.degree. C. to 300.degree. C., for a time period of about 1/2 minute to 30 hours with a water soluble zinc compound in an acidic solution; b) then recovering said polymer. ### Claim 2 (depends on 1) A method according to claim 1 wherein said poly(arylene sulfide/sulfone) polymer is poly(phenylene sulfide/sulfone). ### Claim 3 (depends on 1) A method according to claim 1 wherein said poly(arylene sulfide/sulfone) polymer is produced by reacting a dihaloaromatic sulfone, an alkali metal sulfide, a polar organic compound, with or without water under polymeriztion condtions to form a reaction slurry comprising a poly(arylene sulfide/sulfone) polymer; and then recovering said poly(arylene sulfide/sulfone) from said reaction slurry. ### Claim 4 (depends on 1) A method according to claim 1 wherein said water soluble zinc compound is selected from the group consisting of zinc halides and zinc carboxylates and wherein the concentration of zinc in said acidic solution is 0.01 to 10 weight percent based on the weight of the neat polymer. ### Claim 5 (depends on 4) A method according to claim 4 wherein zinc acetate is said zinc compound. ### Claim 6 (depends on 1) A method according to claim 1 wherein the acidic component of said acidic solution is present in an amount in the range of about 0.01 to 10 weight percent, based on the weight of the polymer. ### Claim 7 (depends on 1) A method according to claim 1 wherein the acid in said acidic solution is selected from the group consisting of acetic acid, oxalic acid, formic acid, and phosphoric acid. ### Claim 8 (depends on 7) A method according to claim 7 wherein the acid in said acidic solution is acetic acid. ### Claim 9 (depends on 1) A method according to claim 1 wherein said recovered polymer is further washed with deionized water. ### Claim 10 (depends on 9) A method according to claim 9 wherein the temperature of said water washing step is in the range of ambient temperature to 250.degree. C. ### Claim 11 A method for treating a poly(arylene sulfide/sulfone) polymer which comprises a) contacting a poly(arylene sulfide/sulfone) polymer with an aqueous acidic solution consisting essentially of zinc acetate in an aqueous acetic acid at a temperature in the range of 40.degree. to 200.degree. C. for a period of 1 minute to 3 hours wherein the concentration of zinc in said acidic solution is in the range of 0.25 to 2 weight percent, based on the weight of said polymer and the acetic acid component is present in an amount of about 0.025 to 5 weight percent of the acidic solution; and then b) recovering the thus treated poly(arylene sulfide/sulfone) polymer. ### Claim 12 A method for treating a poly(arylene sulfide/sulfone) polymer which comprises a) contacting a poly(arylene sulfide/sulfone) polymer with an aqueous acidic solution consisting essentially of zinc acetate in an aqueous phosphoric acid at a temperature in the range of 40.degree. to 200.degree. C. for a period of 1 minute to 3 hours wherein the concentration of zinc in said solution is in the range of 0.25 to 2 weight percent, based on the weight of said polymer and the phosphoric acid component is present in an amount of about 0.025 to 5 weight percent of the acidic solution; and then b) recovering the thus treated poly(arylene sulfide/sulfone) polymer. ### Claim 13 (depends on 1) A poly(arylene sulfide/sulfone) polymer of increased thermal stability and purity treated by the method of claim 1. ### Claim 14 (depends on 11) A poly(arylene sulfide/sulfone) polymer of increased thermal stability and purity prepared by the method of claim 11. ### Claim 15 (depends on 1) A molded article made from a poly(arylene sulfide/sulfone) polymer prepared by the method of claim 1. ### Claim 16 (depends on 1) A composite material which comprises a poly(arylene sulfide/sulfone) polymer prepared according to claim 1 and carbon fibers.