# US 5,350,793 A · Damping material > Agents: this data is available as JSON from the patentgrep API and MCP server — see https://patentgrep.com/llms.txt - Number: US 5,350,793 A - Document ID: US5350793A - Status: Granted - Kind: A - Application number: 07/975,325 - Filed: 1992-11-16 - Granted: 1994-09-27 - Earliest claimed: 1991-11-29 - Assignees: Toda Kogyo Corporation; Hirotani Co., Ltd. - Inventors: Atsunori Kishimoto; Takashi Fujii, deceased; Kazutaka Ohshita; Kazumi Yamamoto; Yasuhiko Fujii; Tetsuro Toda - Web page: https://patentgrep.com/patent/US5350793A ## CPC - C08K 7/00: Use of ingredients characterised by shape - C08K 3/013: Fillers, pigments or reinforcing additives - C08K: Use of inorganic or non-macromolecular organic substances as compounding ingredients (paints, inks, varnishes, dyes, polishes, adhesives C09) ## Abstract Disclosed herein is a damping material comprising: (a) a binder composed of 100 parts by weight of an ethylene-vinyl acetate copolymer containing 30 to 65 wt % of vinyl acetate, and 160 to 330 parts by weight of a petroleum resin containing an aromatic petroleum resin as the main ingredient; and (b) 30 to 180 parts by weight of a filler composed of a scaly powder. ## Claims ### Claim 1 a damping material comprising: (a) a binder composed of 100 parts by weight of an ethylene-vinyl acetate copolymer containing 30 to 65 wt % of vinyl acetate and 160 to 330 parts by weight of a petroleum resin containing an aromatic petroleum resin as the main ingredient based on 100 parts by weight of an ethylene-vinyl acetate copolymer; and (b) 30 to 180 parts by weight of a filler composed of a scaly powder based on 100 parts by weight of said binder. ### Claim 2 (depends on 1) A damping material according to claim 1, wherein said petroleum resin contains not less than 65 wt % of said aromatic petroleum resin. ### Claim 3 (depends on 1) A damping material according to claim 1, wherein the softening point of said petroleum resin is 80.degree. to 170.degree. C. ### Claim 4 (depends on 1) A damping material according to claim 1, wherein said scaly powder is at least one selected from the group consisting of mica, plate-like iron oxide particles and graphite. ### Claim 5 (depends on 1) A damping material according to claim 1, wherein said scaly powder has an average plate diameter of 1 to 2000 .mu.m and an average plate thickness of 0.01 to 100 .mu.m. ### Claim 6 (depends on 1) A damping material according to claim 1, wherein the content of said vinyl acetate is 32 to 65 wt %, the amount of said petroleum resin is 160 to 300 parts by weight based on 100 parts by weight of said ethylene-vinyl acetate copolymer, and the amount of said filler is 70 to 150 parts by weight based on 100 parts by weight of said binder. ### Claim 7 (depends on 1) A damping material according to claim 1, wherein said filler further contains not less than 1 part by weight and less than 50 parts by weight of a granular powder, a fibrous material or a mixture thereof based on 100 parts by weight of said binder. ### Claim 8 (depends on 7) A damping material according to claim 7, which comprises (a) a binder composed of 100 parts by weight of ethylene-vinyl acetate copolymer containing 30 to 65 wt % of vinyl acetate, and 160 to 330 parts by weight of the petroleum resin containing an aromatic petroleum resin as the main ingredient based on 100 parts by weight of an ethylene-vinyl acetate copolymer; and (b) 31 to 180 parts by weight of the filler composed of the scaly powder and the granular powder, the fibrous material or the mixture thereof, the amount of said scaly powder being 30 to 150 parts by weight based on 100 parts by weight of said binder, the amount of said granular powder, said fibrous material or the mixture thereof being not less than 1 part by weight and less than 50 parts by weight, and the total amount of said scaly powder, said granular powder and said fibrous material being 31 to 180 parts by weight based on 100 parts by weight of said binder. ### Claim 9 (depends on 7) A damping material according to claim 7, wherein said granular powder has an average particle diameter of 0.05 to 100 82 m, and said fibrous material is fibrous, acicular or spindle-shaped material having an average major axial diameter of 0.1 to 50,000 .mu.m, an average minor axial diameter of 0.02 to 250 .mu.m, and an aspect ratio of not less than 3.0. ### Claim 10 (depends on 9) A damping material according to claim 9, wherein said granular powder is at least one selected from the group consisting of hematite particles, magnetite particles, maghemite particles, strontium ferrite particles, barium ferrite particles, quarts sand, talc, clay, lead powder, iron powder, titanium oxide, zinc white, barium sulfate and calcium carbonate. ### Claim 11 (depends on 9) A damping material according to claim 9, wherein said fibrous material is at least one selected from the group consisting of magnetite, maghemite, a synthetic fiber, asbesto, a natural organic fiber, a glass fibers and a carbon fiber. ### Claim 12 (depends on 8) A damping material according to claim 8, wherein the content of said vinyl acetate is 32 to 65 wt %, the amount of said petroleum resin is 160 to 300 parts by weight based on 100 parts by weight of said ethylene-vinyl acetate copolymer, the amount of said scaly powder is 50 to 150 parts by weight based on 100 parts by weight of said binder, the amount of said granular powder, said fibrous material or a mixture thereof is 1 to 40 parts by weight based on 100 parts by weight of said binder, and the total amount of said scaly powder, said granular powder, said fibrous material or a mixture thereof is 70 to 150 parts by weight based on 100 parts by weight of said binder.