# US 5,350,718 A · Glass frits, a process for their production and their use in enamel barrier layers for stopping the migration of silver > Agents: this data is available as JSON from the patentgrep API and MCP server — see https://patentgrep.com/llms.txt - Number: US 5,350,718 A - Document ID: US5350718A - Status: Granted - Kind: A - Application number: 08/115,034 - Filed: 1993-09-01 - Granted: 1994-09-27 - Earliest claimed: 1991-03-25 - Assignees: Degussa AG - Inventors: Jerome Anquetil; Alain Dauger - Web page: https://patentgrep.com/patent/US5350718A ## CPC - C03C 8/02: Frit compositions, i.e. in a powdered or comminuted form - C03C 8/04: containing zinc - C03C 17/04: by fritting glass powder - C03C 17/3411: {with at least two coatings of inorganic materials (C03C17/36, C03C17/42 take precedence)} - C03C: CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS ## Abstract Glass frits are disclosed which are essentially free of lead and contain 0.05 to 15 mol-% sulfur and/or sulfides, preferably zinc sulfide. A process is disclosed for producing a glass frit by melting a mixture of oxides and/or non-oxide compounds (fluorides, carbonates) at temperatures of 1,000.degree. to 1,300.degree. C., followed by sudden cooling, characterized in that the glass frit contains between 0.05 and 15 mol-% sulfur, zinc sulfide or other sulfides. The glass frits can be used in enamel barrier layers for stopping the migration of silver. ## Claims ### Claim 1 A glass frit essentially free of lead for forming an enamel capable of preventing Ag.sup.+ migration, said glass frit comprising 15 to 70% by weight zinc oxide, 15 to 40% by weight silicon dioxide and 5 to 25% by weight boron trioxide and containing dissolved in said glass 0.05 to 15 mol % of at least one member of the group consisting of sulfur and sulfides. ### Claim 2 (depends on 1) The glass frit according to claim 1, wherein said sulfide is zinc sulfide. ### Claim 3 (depends on 1) The glass frit according to claim 1, wherein 30 to 65% by weight of said zinc oxide is present. ### Claim 4 (depends on 1) The glass frit according to claim 1, further comprising coloring metal oxides. ### Claim 5 (depends on 1) The glass frit according to claim 1 which is colorless. ### Claim 6 (depends on 1) The glass frit according to claim 1, wherein said sulfide is at least one member of the group consisting of sulfides of alkali metals, alkaline earth metals, Mn, Fe, Co, Ni, Cu, Cd, Sn, Sb, and Bi. ### Claim 7 A glass surface having deposited thereon an enamel barrier layer which stops the migration of silver, said layer being formed from a glass frit and optionally one or more colorants and/or opacifiers, said glass frit is essentially free of lead for forming an enamel capable of preventing Ag.sup.+ migration, said glass frit comprising 15 to 70% by weight zinc oxide, 15 to 40% by weight silicon dioxide and 5 to 25% by weight boron trioxide and containing dissolved in said glass 0.05 to 15 mol % of at least one member of the group consisting of sulfur and sulfides. ### Claim 8 (depends on 7) The enamel barrier layer according to claim 7, wherein said sulfide is zinc sulfide. ### Claim 9 (depends on 7) The enamel barrier layer according to claim 7, further comprising coloring metal oxides. ### Claim 10 (depends on 7) The enamel barrier layer according to claim 7, wherein said sulfide is at least one member of the group consisting of sulfides of alkali metals, alkaline earth metals, Mn, Fe, Co, Ni, Cu, Cd, Sn, Sb, and Bi. ### Claim 11 A method of preventing silver migration into glass comprising placing an enamel barrier layer formed from glass frit and optionally one or more colorants and/or opacifiers between sheet glass and a resistive layer containing silver and firing at a temperature of from 450.degree. C. to 800.degree. C., wherein said glass frit is essentially free of lead for forming an enamel capable of preventing Ag.sup.+ migration, said glass frit comprising 15 to 70% by weight zinc oxide, 15 to 40% by weight silicon dioxide and 5 to 25 % by weight boron trioxide and containing dissolved in said glass 0.05 to 15 mol % of at least one member of the group consisting of sulfur and sulfides. ### Claim 12 (depends on 11) The method according to claim 11, wherein said temperature is from 550.degree. C. to 750.degree. C. ### Claim 13 A composite glass product comprising sheet glass, enamel barrier layer, and silver resistive layer made by a method comprising placing an enamel barrier layer formed from a glass frit and optionally one or more colorants and/or opacifiers between sheet glass and a resistive layer containing silver and firing at a temperature of from 450.degree. C. to 800.degree. C., wherein said glass frit is essentially free of lead for forming an enamel capable of preventing Ag.sup.+ migration said glass frit comprising 15 to 70% by weight zinc oxide, 15 to 40% by weight silicon dioxide and 5 to 25% by weight boron trioxide and containing dissolved in said glass 0.05 to 15 mol % of at least one member of the group consisting of sulfur and sulfides. ### Claim 14 A composite glass article comprising a glass support layer, an enamel barrier layer deposited on said glass support layer, and a silver resistive layer deposited on said barrier layer, said enamel barrier layer being formed from a glass frit and optionally one or more colorants and/or opacifiers, wherein said glass frit is essentially free of lead for forming an enamel capable of preventing Ag.sup.+ migration, said glass frit comprising 15 to 70% by weight zinc oxide, 15 to 40% by weight silicon dioxide and 5 to 25% by weight boron trioxide and containing dissolved in said glass 0.05 to 15 mol % of at least one member of the group consisting of sulfur and sulfides. ### Claim 15 (depends on 14) The composite glass article according to claim 14 which is glass for an automobile. ### Claim 16 A process for the production of a glass frit essentially free of lead for forming an enamel capable of preventing Ag.sup.+ migration, said glass frit comprising 15 to 70% by weight zinc oxide, 15 to 40% by weight silicon dioxide and 5 to 25% by weight boron trioxide and containing dissolved in said glass 0.05 to 15 mol % of at least one member of the group consisting of sulfur and sulfides, said process comprises melting a mixture comprising (a) glass forming oxide compounds, or non-oxide compounds which form glass forming oxides, corresponding to 15 to 70% by weight zinc oxide, 15 to 40% by weight silicon dioxide and 5 to 25% by weight boron trioxide and (b) 0.05 to 15 mol % of at least one member of the group consisting of sulfur and sulfides, at a temperature of 1,000.degree. to 1,300.degree. C. to dissolve said sulfur or said sulfides in said glass, cooling suddenly to form granules, and grinding said granules to form a frit. ### Claim 17 A glass frit essentially free of lead for forming an enamel capable of preventing Ag.sup.+ migration, said glass frit comprising 15 to 70% by weight zinc oxide, 15 to 40% by weight silicon dioxide and 5 to 25% by weight boron trioxide and containing dissolved in said glass 0.05 to 15 mol % of at least one member of the group consisting of sulfur and sulfides; said glass frit being produced by a process comprising melting a mixture comprising (a) glass forming oxide compounds, or non-oxide compounds which form glass forming oxides, corresponding to 15 to 70% by weight zinc oxide, 15 to 40% by weight silicon dioxide and 5 to 25% by weight boron trioxide and (b) 0.05 to 15 mol % of at least one member of the group consisting of sulfur and sulfides, at a temperature of 1,000.degree. to 1,300.degree. C. to dissolve said sulfur or said sulfides in said glass, cooling suddenly to form granules, and grinding said granules to form a frit.