# US 5,350,471 A · Production of cross-laminated film from tube > Agents: this data is available as JSON from the patentgrep API and MCP server — see https://patentgrep.com/llms.txt - Number: US 5,350,471 A - Document ID: US5350471A - Status: Granted - Kind: A - Application number: 08/055,580 - Filed: 1993-05-03 - Granted: 1994-09-27 - Earliest claimed: 1993-05-03 - Inventors: Mirek Planeta - Web page: https://patentgrep.com/patent/US5350471A ## CPC - B29C 55/28: of blown tubular films, e.g. by inflation {(extrusion moulding of tubular films B29C48/03)} - B29C 48/0022: {combined with cutting} - B29C 53/10: of blown tubular films, e.g. gusseting {(flattening blown films during extrusion moulding B29C48/03)} - B29C 48/0018: {combined with shaping by orienting, stretching or shrinking, e.g. film blowing (B29C48/0017 takes precedence)} - B29C 48/0019: {combined with shaping by flattening, folding or bending} - B29C 48/10: flexible, e.g. blown foils - B29C 48/21: the layers being joined at their surfaces - B29C 48/355: Conveyors for extruded articles - B29C 2793/0063: Cutting longitudinally - B29L 2009/00: Layered products - Y10S 264/81: Plastic net - Y10T 156/1067: Continuous longitudinal slitting - Y10T 156/1087: Continuous longitudinal slitting - B29C: SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING (making preforms B29B11/00; making laminated products by combining previously unconnected layers which become one product whose layers will remain together B32B37/00 - B32B41/00) - B29L: INDEXING SCHEME ASSOCIATED WITH SUBCLASS B29C, RELATING TO PARTICULAR ARTICLES - Y10S: TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS - Y10T: TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION ## Abstract A cross-oriented multi-layer laminated plastic film is produced by first providing a flattened tubular plastic film having a outer plastic film layer with a first melting temperature and an inner plastic film layer with a second melting temperature lower than the first melting temperature, the outer plastic film layer having a molecular orientation substantially in the direction of the length of the tubular plastic film. The flattened tubular plastic film is passed from an expanding station in an expanded condition along a predetermined path in the direction of the length of said film to a collapsing station in a continuous manner. The expanded tubular plastic film is rotated about the predetermined path as the film passes from the expanding station to the collapsing station to effect cross-orientation of the outer film layer in directions inclined to the direction of travel of the tubular plastic film. The tubular plastic film is flattened at the collapsing station and pressure is applied to the flattened film at a temperature high enough to soften the inner plastic film but low enough not to soften the outer plastic film layer to an extent to cause the outer plastic film layer to lose its molecular orientation. The said pressure causes the opposite sides of the tubular plastic film to engage one another and to cause adjacent inner film layers to become bonded together and to the outer film layers to form a cross-oriented multi-layer laminated plastic film. ## Claims ### Claim 1 A method of producing a cross-oriented multi-layer laminated plastic film comprising; providing a flattened tubular plastic film having a outer plastic film layer with a first melting temperature and an inner plastic film layer with a second melting temperature lower than the first melting temperature, said outer plastic film layer having a molecular orientation substantially in the direction of the length of the tubular plastic film, passing said flattened tubular plastic film from an expanding station in an expanded condition along a predetermined path in the direction of the length of said film to a collapsing station in a continuous manner, rotating the expanded tubular plastic film about the predetermined path as the film passes from the expanding station to the collapsing station to effect cross-orientation of the outer film layer in directions inclined to the direction of travel of the tubular plastic film, and flattening the tubular plastic film at the collapsing station and applying pressure to the flattened film at a temperature high enough to soften the inner plastic film layer but low enough not to soften the outer plastic film layer to an extent to cause the outer plastic film layer to loose its molecular orientation, said pressure causing the opposite sides of the tubular plastic film to engage one another and to cause adjacent inner film layers to become bonded together and to the outer film layers to form a cross-oriented multi-layer laminated plastic film. ### Claim 2 (depends on 1) A method according to claim 1 wherein said expanding station is stationary and said collapsing station is rotated to effect said cross-orientation. ### Claim 3 (depends on 2) A method according to claim 2 wherein said flattened tubular plastic film is provided by continuously co-extruding said outer film layer and inner film layer from an annular co-extrusion die to produce a tubular plastic film in an expanded condition, collapsing the tubular plastic film to a flattened condition, and passing the flattened tubular plastic film to the expanding station. ### Claim 4 (depends on 1) A method according to claim 1 wherein said expanding station is rotated to effect said cross-orientation and said collapsing station is stationary. ### Claim 5 (depends on 4) A method according to claim 4 wherein said flattened tubular plastic film is provided as a roll of said film at the expanding station. ### Claim 6 (depends on 1) A method according to claim 1 wherein the outer plastic film layer is of a readily molecularly oriented material selected from the group consisting of high density polyethylene, polypropylene, linear low density polyethylene, nylon, polyester, polystyrene, polyvinyl chloride and polyvinylidenechloride. ### Claim 7 (depends on 1) A method according to claim 1 wherein the outer plastic film layer has a thickness in the range of from about 0.1 to about 4 mils. ### Claim 8 (depends on 7) A method according to claim 7 wherein the outer plastic film layer is of high density polyethylene. ### Claim 9 (depends on 1) A method according to claim 1 wherein the inner plastic film layer is of a bonding material selected from the group consisting of ethyl vinyl acetate low density polyethylene, linear low density polyethylene and ethyl propyl terpolymer. ### Claim 10 (depends on 1) A method according to claim 1 wherein the inner plastic film layer has a thickness in the range of from about 0.05 to about 1.0 mils. ### Claim 11 (depends on 10) A method according to claim 10 wherein the inner plastic film layer is of ethyl vinyl acetate. ### Claim 12 (depends on 1) A method according to claim 1 wherein said rotation effects cross-orientation with an angle between the orientation axes of the outer film layers in the direction of the length of the tubular plastic film in the range of from about 10.degree. to about 90.degree.. ### Claim 13 (depends on 1) A method according to claim 1 wherein said flattened tubular plastic film provided has a further bonding plastic film layer external to the outer plastic film layer and having a melting temperature lower than the melting temperature of the outer plastic film layer, said external plastic film layers being bonded to the outer plastic film layers in the resultant cross-oriented multi-layer laminated plastic film. ### Claim 14 (depends on 1) A method according to claim 1 including slitting the tubular plastic film into longitudinally extending ribbons as it is passed in an expanded condition to the collapsing station.